Disertación de Maestría
DOI
10.11606/D.74.2018.tde-20112018-104011
Documento
Autor
Nombre completo
Rafael Henrique Filomeno
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2018
Director
Tribunal
Rossignolo, João Adriano (Presidente)
Dias, Cleber Marcos Ribeiro
Souza, Rui Barbosa de
Tonin, Fernando Gustavo
Título en portugués
Avaliação da influência da umidade relativa da atmosfera de cura na carbonatação de materiais de fibrocimento
Palabras clave en portugués
Carbonatação
Compósitos
Durabilidade
Polpas celulósicas
Umidade atmosférica
Resumen en portugués
A carbonatação acelerada é um processo químico que têm se tornado muito atrativa para a indústria do fibrocimento, por mitigar a degradação das fibras vegetais utilizadas nos materiais e por melhorar o desempenho físico-mecânico dos compósitos. Nesse contexto, o presente trabalho avaliou a influência da umidade no processo de carbonatação acelerada, em fibrocimentos reforçados com polpas celulósicas de eucalipto. Para o desenvolvimento das atividades experimentais foi realizado primeiramente um estudo da evolução da carbonatação nos compósitos de fibrocimento, considerando diferentes concentrações de umidade relativa (60, 70, 80 e 90%). Posteriormente, foi realizada a caracterização dos compósitos de fibrocimento por meio da avaliação do desempenho físico-mecânico, com ensaio mecânico de flexão em quatro pontos que determinou o módulo de ruptura (MOR), módulo elástico (MOE), limite de proporcionalidade (LOP) e energia específica (EE); e ensaios físicos para obtenção dos valores de absorção de água (AA), densidade aparente (DA) e porosidade aparente (PA). Os compósitos foram também avaliados quanto à durabilidade e microestrutura, através de ensaios de envelhecimento acelerado, composição mineralógica e análise microestrutural. A partir dos resultados obtidos, os compósitos carbonatados com 60% de umidade relativa apresentaram maior formação de carbonato de cálcio, maior densificação da matriz cimentícia e, consequentemente, menor quantidade de espaços vazios logo nas primeiras horas de carbonatação. Em relação ao desempenho dos compósitos de fibrocimento, as umidades de 60 e 70% permitiram que a carbonatação proporcionasse maiores valores de MOR, LOP e MOE, diferindo estatisticamente dos demais compósitos. Os ensaios físicos complementaram os ensaios mecânicos, mostrando que os compósitos carbonatados com 60 e 70% de umidade apresentaram menores valores de AA e PA, junto de maiores valores de DA. O processo de carbonatação acelerada foi favorecido pelas menores concentrações de umidade relativa, como apresentado também pelas análises de TG e DRX, que permitiram que o processo acontecesse de forma mais efetiva, melhorando a interface fibra-matriz.
Título en inglés
Evaluation of the relative humidity influence of the curing atmosphere on the carbonation of fiber-cement materials
Palabras clave en inglés
Atmospheric humidity
Carbonation
Cellulosic pulps
Composites
Durability
Resumen en inglés
The accelerated carbonation is a process that can be made very feasible for the fiber cement industry, for mitigating the degradation of the vegetable fibers used in the materials and for improving the physico-mechanical performance of composites. In this context, the present work evaluated the influence of relative humidity in the accelerated carbonation process in fiber cement composites reinforced with eucalyptus cellulosic pulps. For the development of experimental activities, a study of the evolution of carbonation in fiber cement composites was carried out, considering different concentrations of relative humidity (60, 70, 80 e 90%). Subsequently, the characterization of fiber cement composites was evaluated through the physical-mechanical performance evaluation, with a four-point mechanical test that determined the modulus of rupture, modulus of elasticity, limit of proportionality and specific energy; and physical tests to obtain the values of water absorption, bulk density and apparent void volume. The composites were also evaluated for durability and microstructure, through accelerated aging, mineralogical composition and microstructural analysis. From the results obtained, the carbonate composites with 60% relative humidity showed a higher calcium carbonate formation, a higher densification of the cementitious matrix and, consequently, a lower amount of voids in the first few hours of carbonation. In relation of the performance of fiber cement composites, the 60 and 70% humidity allowed the carbonation to provide higher values of mechanical analysis, differing statistically from the other composites. The physical tests complemented the mechanical tests, showing that the carbonated composites with 60 and 70% humidity presented lower values of water absorption and apparent void volume, with a greater filling of the empty spaces of the composites. The accelerated carbonation process was favored by the lower concentrations of relative humidity, as also shown by the TG and XRD analyzes, which allowed the process to happen more effectively, improving the fiber-matrix interface.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
ME6908177COR.pdf (3.57 Mbytes)
Fecha de Publicación
2018-11-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.