Disertación de Maestría
DOI
https://doi.org/10.11606/D.74.2021.tde-15102021-122328
Documento
Autor
Nombre completo
Alda Renata dos Santos Martinho Capelo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2021
Director
Tribunal
Rossignolo, João Adriano (Presidente)
Akasaki, Jorge Luís
Santos, Sérgio Francisco dos
Título en portugués
Cimento à base de óxido de magnésio e cinza da casca do arroz
Palabras clave en portugués
Alcalinidade
CCA
Cimento magnesiano
Pozolana
Sílica reativa
Resumen en portugués
Em certas aplicações técnicas, as fibras celulósicas são usadas em matrizes cimentícias para a produção de compósitos. No entanto, sua utilização é limitada devido à precoce degradação causada pela elevada alcalinidade do meio, quando a matriz é a base de cimento Portland. Deste modo, a presente pesquisa avaliou como solução alternativa a reação da sílica originária da cinza da casca do arroz (CCA) em presença do óxido de magnésio (MgO), para a produção de cimento magnesiano de reduzida alcalinidade. Foram produzidas cinzas com diferentes tratamentos térmicos, diferindo nas temperaturas de 500, 550, 600 e 650 °C e submetidas a uma avaliação inicial da pozolanicidade por meio da condutividade elétrica. Foram preparadas pastas com formulação 50% MgO-50% CCA, expostas a cura térmica em diferentes idades, sobre as quais se realizaram as análises de difratometria de raios X (DRX), termogravimetria (TG) e avaliação do pH. Com a cinza de maior reatividade foram produzidas pastas em 3 formulações (60% MgO-40% CCA, 70% MgO-30% CCA e 80% MgO-20% CCA). Por fim, se moldaram corpos de prova cilíndricos e submetidos ao ensaio de compressão axial. A cinza produzida a 500 oC foi a que se mostrou mais reativa, com condutividade elétrica final de 800 µS/cm e perda de massa residual de 82,11%, na idade inicial, o que se refletiu na maior formação do composto MSH pela presença da região mais amorfa e menor pH, (entre 9,62 e 9,94) ao longo do tempo. Os resultados do ensaio de compressão axial mostram de modo geral que não houve diferença estatística na resistência mecânica entre a CCA 500 e SA. Com valores de 19,02 15,90 MPa respetivamente, para a formulação 50% MgO-50% CCA.
Título en inglés
Cement based on magnesium oxide and rice husk ash
Palabras clave en inglés
Alkalinity
CCA
Magnesian cement
Pozzolana
Reactive silica
Resumen en inglés
In certain technical applications, cellulosic fibers are used in cementitious matrices to produce composites. However, its use is limited due to the early degradation caused by the high alkalinity of the medium, when the matrix is based on Portland cement. Thus, the present research evaluated as an alternative solution the reaction of silica originating from rice husk ash (CCA) in the presence of magnesium oxide (MgO), for the production of low alkalinity magnesian cement. Ashes were produced with different heat treatments, differing at temperatures of 500, 550, 600 and 650 °C and submitted to an initial evaluation of pozzolanicity by means of electrical conductivity. Pastes were prepared with a 50% MgO-50% CCA formulation, exposed to thermal curing at different ages, on which X-ray diffractometry (DRX), thermogravimetry (TG) and pH evaluation were analyzed. With the highest reactivity ash, pastes were produced in 3 formulations (60% MgO-40% CCA, 70% MgO-30% CCA and 80% MgO-20% CCA). Finally, cylindrical specimens were molded and submitted to the axial compression test. Ash produced at 500 oC was the most reactive, with final electrical conductivity of 800 µS/cm and loss of residual mass of 82.11% at initial age, which was reflected in the greater formation of the MSH compound by the presence of the more amorphous region and lower pH, (between 9.62 and 9.94) over time. The results of the axial compression test show, in general, that there was no statistical difference in mechanical strength between CCA 500 and SA. With values of 19.02 to 15.90 MPa, respectively, for the 50% MgO-50% CCA formulation.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
ME10650064COR.pdf (2.61 Mbytes)
Fecha de Publicación
2021-10-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.