• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
https://doi.org/10.11606/T.74.2020.tde-13042021-132215
Documento
Autor
Nombre completo
Kátia Helena dos Santos
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2020
Director
Tribunal
Pallone, Eliria Maria de Jesus Agnolon (Presidente)
Alves Junior, Clodomiro
Colnago, Luiz Alberto
Lobo, Anderson de Oliveira
Osiro, Denise
Título en portugués
Influência do tratamento por plasma frio na formação de fosfatos de cálcio sobre a superfície do nanocompósito de Al2O3/ZrO2
Palabras clave en portugués
Al2O3/ZrO2
Nanocompósito
Plasma frio
Recobrimento biomimético
Tratamento superficial
Resumen en portugués
Devido à natureza bioinerte do nanocompósito de alumina/zircônia (Al2O3/ZrO2), recobrimentos superficiais com fosfatos de cálcio são utilizados para melhorar a sua interação com o tecido hospedeiro quando implantado. Visando melhorar a interface nanocompósito/fosfatos, tratamentos superficiais antes do recobrimento são realizados. Nesse sentido, o tratamento por plasma frio se destaca por promover modificações apenas nas propriedades químicas e físicas superficiais do nanocompósito, sem comprometer as suas características intrínsecas. Assim, o objetivo desse trabalho foi avaliar a influência do tratamento por plasma frio na formação de fosfatos de cálcio sobre a superfície do nanocompósito de Al2O3/ZrO2. Para isso, nanocompósitos de Al2O3 contendo 5 % em volume de inclusões nanométricas de ZrO2 foram conformados por prensagem isostática e sinterizados à 1500 °C por 2 h. Em seguida, foram tratados superficialmente usando diferentes proporções de fluxo dos gases de nitrogênio (N2) e oxigênio (O2). O fluxo do gás de hidrogênio (H2) foi mantido constante 50 %. Após essa etapa, os nanocompósitos tratados e não tratado superficialmente foram recobertos biomimeticamente com fosfatos de cálcio durante 14 dias, e então caracterizados usando diferentes técnicas. Os resultados obtidos mostraram que o prévio tratamento, independentemente da atmosfera gasosa, afetou quimicamente aos grupos funcionais superficiais da ZrO2 e da Al2O3 nos nanocompósitos. Observou-se ainda que apesar das espécies ativas do gás N2 ser predominante, as espécies ativas do gás O2 também promoveram alterações nesses grupos funcionais superficiais. Ressalta-se que o tratamento favoreceu a formação de três fases de fosfatos de cálcio: α e β-fosfato tricálcico (α e β-TCP) e hidroxiapatita (HA). Além disso, o percentual dessas fases variou em função das diferentes proporções gasosas usadas no tratamento superficial por plasma frio. Dentre as condições estudadas, as superfícies tratadas com maior proporção do fluxo do gás N2 apresentaram maior formação de fosfatos de cálcio. Os testes in vitro demonstraram que os nanocompósitos tratados e recobertos são biocompatíveis, se mostrando promissores para serem usados como substitutos ósseos.
Título en inglés
Influence of cold plasma treatment on the formation of calcium phosphates on the surface of the Al2O3/ZrO2 nanocomposite
Palabras clave en inglés
Al2O3/ZrO2
Biomimetic coating
Cold plasma
Nanocomposite
Surface treatment
Resumen en inglés
Due to the bioinert nature of the alumina/zirconia (Al2O3/ZrO2) nanocomposite, surface coatings with calcium phosphates are used to improve their interaction with the host tissue when implanted. In order to improve the nanocomposite/phosphate interface, surface treatments before coating have been carried out. In this sense, cold plasma treatment stands out for promoting changes only in the surface chemical and physical properties of the nanocomposite, without compromising its intrinsic characteristics. Thus, the objective of this work was to evaluate the influence of cold plasma treatment on the formation of calcium phosphates on the surface of the Al2O3/ZrO2 nanocomposite. For this, Al2O3 nanocomposites containing 5 % by volume of ZrO2 nanometric inclusions were formed by isostatic pressing and sintered at 1500 °C for 2 h. Then, they were superficially treated using different flow rates of nitrogen (N2) and oxygen (O2) gases. The H2 gas flow was maintained at 50 %. After this stage, the nanocomposites treated and untreated superficially were coated biomimetically with calcium phosphates for 14 days, and then characterized using different techniques. The results obtained showed that the previous treatment, regardless of the gaseous atmosphere, chemically affected the surface functional groups of ZrO2 and Al2O3 in the nanocomposites. It was also observed that although the active species of N2 gas are predominant, the active species of O2 gas also promoted changes in these superficial functional groups. It should be noted that the treatment favored the formation of three phases of calcium phosphates: α-tricalcium phosphate (α-TCP), and β-tricalcium phosphate (β-TCP) and hydroxyapatite (HA). In addition, the percentage of these phases varied according to the different gas proportions used in the cold plasma surface treatment. Among the conditions studied, the surfaces treated with a greater proportion of the N2 gas flow showed greater formation of calcium phosphates. In vitro tests have shown that the treated and coated nanocomposites are biocompatible, showing promise for use as bone substitutes.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
DO8845571COR.pdf (4.52 Mbytes)
Fecha de Publicación
2021-04-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.