Thèse de Doctorat
DOI
10.11606/T.59.2009.tde-16062009-134859
Document
Auteur
Nom complet
Márcio José dos Reis
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2009
Directeur
Jury
Valim, Joao Barros (Président)
Bizeto, Marcos Augusto
Davolos, Marian Rosaly
Naal, Zeki
Oliveira, Herenilton Paulino
Titre en portugais
Síntese e caracterização de hidróxidos duplos lamelares preparados na presença de polímeros orgânicos ou com macromoléculas intercaladas
Mots-clés en portugais
Compósitos orgânico-inorgânicos
Compostos lamelares
Hidróxido duplo lamelar
Materiais
Resumé en portugais
Compostos lamelares do tipo da hidrotalcita ou hidróxidos duplos lamelares (HDL), são materiais que possuem notáveis propriedades estruturais, químicas, eletrônicas, iônicas, ópticas e magnéticas. Em função dessas propriedades, os HDL apresentam uma diversidade de aplicações tais como adsorventes e catalisadores. Este trabalho tem por objetivo utilizar polímeros e macromoléculas na preparação e caracterização de HDL, visando melhorar as propriedades texturais dos HDL de MgAl-CO3 preparados em meio contendo polímeros orgânicos ou a intercalação direta de dendrímeros tipo PAMAM de gerações -0,5 e +0,5 em HDL do sistema Zn/Al. Os HDL de MgAl-CO3 foram preparados pela adaptação do método de coprecipitação a pH decrescente, com a presença de polímeros solubilizados no meio, como molde. Os materiais foram caracterizados por difração de Raios X, análise termogravimétrica, espectroscopia no infravermelho e medidas de área superficial por BET. Baseando-se nos resultados obtidos, pode-se concluir que propriedades texturais dos HDL preparados são modificadas, quando na presença de alguns polímeros. Na maioria dos casos, os valores calculados de área superficial específica foram mais elevados, em comparação com aquele obtido para o HDL preparado em meio reacional sem polímero. Isto pode ser explicado pela diminuição do tamanho de partículas e aumento no diâmetro médio de poros dos materiais preparados, provocada pela presença de polímeros no meio reacional. Os HDL intercalados com dendrímeros PAMAM G-0,5 e PAMAM G+0,5 foram preparados por duas rotas diferentes: coprecipitação a pH constante e troca iônica em fase dupla. Os materiais obtidos foram caracterizados por meio de difração de Raios X, análise de termogravimétrica associada à espectrometria de massas e espectroscopia no infravermelho. Utilizando os dois procedimentos de preparação, a intercalação de PAMAM G-0,5 deu origem a HDL com os mesmos espaçamentos basais, concordando com a intercalação dos ânions do dendrímero em um arranjo perpendicular à lamela do HDL, enquanto que para a intercalação do PAMAM G+0,5, espaçamentos basais muito menores do que o tamanho da molécula foram obtidos. A diferença entre a distância interlamelar observada e a esperada pode ser explicada por um arranjo peculiar das moléculas desse dendrímero em uma forma elipsoidal, devido às interações intramoleculares. Espectros no infravermelho confirmam a presença dos dendrímeros nos materiais Zn2Al-PAMAM G-0,5 e Zn2Al-PAMAM G+0,5. Finalmente, a presença destes dendrímeros foi confirmada por análise térmica associada com espectrometria de massas. Os estudos de Raios X com variação de temperatura in situ e as análises termogravimétricas revelaram que o material obtido pela intercalação do PAMAM G+0,5 é termicamente menos estável do que aquele intercalado com PAMAM G-0,5, concordando com a diferença de estabilidade entre os dendrímeros livres.
Titre en anglais
Synthesis and characterization of layered double hydroxides prepared in the presence of organic polymers or intercalated with macromolecules
Mots-clés en anglais
hybrid materials
Lamellar compounds
Layered double hydroxides
organic-inorganic compounds
Resumé en anglais
Hydrotalcite-like lamellar compounds or layered double hydroxides (LDH) are materials that present notable structural, chemical, electronic, ionic, optical and magnetic properties. Depending on these properties, the LDH present a great variety of applications such as adsorbents and catalysts. The aim of this work is to prepare and to characterize MgAl-CO3-LDH prepared in aqueous media containing organic polymer to improve textural properties, and to prepare HDL by intercalation of dendrimer (PAMAM) of generations -0.5 and +0.5 in ZnAl-HDL. MgAl-CO3-HDL samples were prepared by an adaptation of the coprecipitation method at decreasing pH, with the presence of polymers in the aqueous media as template. The materials were characterized by powder X-ray diffraction, termogravimetric analysis, infrared spectroscopy and BET isotherms. Based on the obtained results, it can be concluded that the textural properties of the prepared LDH were modified. The calculated values of specific surface area were higher in most of the cases compared with those obtained by the LDH prepared without polymer due to a decrease of the particle size and an increase in the average pore diameter of the prepared materials due to the presence of polymers. HDL with intercalated (PAMAM) dendrimers G-0.5 and G+0.5 were prepared by two different methods: coprecipitation at constant pH, and ionic exchange in double phase. The obtained materials were characterized by powder X-ray diffraction, thermal gravimetric analysis associated with mass spectrometry, and infrared spectroscopy. X-ray powder diffraction patterns exhibit the characteristic profiles of the lamellar materials with basal spacing depending on the nature of the dendrimer. For both preparation methods, the intercalation of PAMAM G-0.5 gives rise to LDH with basal spacing in agreement with the dendrimer molecules perpendicular to the layer of the host structure, while for PAMAM G+0.5 a basal spacing smaller than the molecule size was obtained. The difference between the obtained and the expected value is explained by an accommodation of the dendrimer molecule in an ellipsoidal shape, due to the intra-molecular interactions. Infrared spectra confirm the presence of dendrimers in the Zn2Al-PAMAM G-0.5 and Zn2Al-PAMAM G+0.5 materials. Finally, thermal analyses associated with mass spectrometry confirm the presence of these dendrimers. Powder X-ray diffraction with in situ temperature variation reveals that the material obtained by the PAMAM G+0.5 intercalation is thermally less stable than that prepared by PAMAM G-0.5 intercalation, in agreement with the difference in the thermal stability of the free dendrimers.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TESE.pdf (1.89 Mbytes)
Date de Publication
2009-07-21
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.