Disertación de Maestría
DOI
10.11606/D.59.2005.tde-04082005-183118
Documento
Autor
Nombre completo
Ernando Silva Ferreira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2005
Director
Tribunal
Mulato, Marcelo (Presidente)
Ito, Amando Siuiti
Marques, Francisco das Chagas
Título en portugués
"Filmes finos de brometo de tálio (TlBr) produzidos por spray pyrolysis".
Palabras clave en portugués
Brometo de tálio
Difração de raios-X
Filmes finos
Microscopia eletrônica de varredura
Resumen en portugués
Neste trabalho é apresentado o estudo de alguns dos principais parâmetros envolvidos na fabricação de filmes finos de brometo de tálio (TlBr) por meio da técnica de spray pyrolysis. Investigamos a possibilidade desta técnica vir a se tornar um método alternativo para fabricação de filmes finos de TlBr com qualidade adequada para a confecção de dispositivos detectores de radiação de altas energias, como raios-X e raios-γ. O tempo de fabricação e a qualidade dos filmes eram limitados pelo problema da formação de gotas d’água na parte superior da câmara de deposição, o que resultava na incidência destas gotas sobre os filmes, posteriormente. O problema foi resolvido por meio de um sistema de aquecimento extrínseco ao equipamento. A investigação dos parâmetros citados se deu pela variação dos fluxos de nitrogênio e da solução de TlBr, pelas variações da posição dos substratos no porta substrato, da temperatura e do grau de saturação das soluções. As propriedades cristalinas e estruturais dos filmes foram verificadas pela técnica de difração de raios-X e por microscopia eletrônica de varredura, respectivamente. Os resultados mostram que o pico de intensidade dos planos cristalinos preferenciais dos filmes tendem a se tornar mais intensos para soluções saturadas, fabricados com baixo fluxo de nitrogênio e a temperaturas próximas de 100oC. No entanto, dependendo da posição dos filmes sobre o porta-substrato, a intensidade dos picos, assim como a rugosidade superficial, variam significativamente. Com efeito, conseguimos estender o processo de deposição para qualquer tempo desejado, o que implica, a princípio, em filmes mais espessos e de melhor qualidade.
Título en inglés
Thin films of thallium bromide (TlBl) manufectured by spray pyrolysis
Palabras clave en inglés
MEV
thallium bromide
thin films
x-ray diffraction
Resumen en inglés
This work presents the results about the investigation of the importance of some of the main parameters related to the fabrication of thin films of thallium bromide (TlBr) using the spray pyrolysis technique. We evaluated the possibilities for the future use of this technique in the development of high quality TlBr thin films to be used as high-energy radiation (such as X- and gamma rays) detectors. The total deposition time as well as the quality of the films were limited due to the formation of water droplets at the inner part of the top surface of the deposition chamber. These droplets would eventually fall over the substrates damaging the sample. This problem was solved by the use of an external heating system. The investigated deposition parameters were: nitrogen and solution flows, substrate position on top of the substrate holder, deposition temperature and composition of the solution. The crystalline and structural properties of the thin films were investigated by X-ray diffraction and Scanning Electron Microscopy. According to the results obtained from the diffraction experiments, the crystalline peaks increase with the saturation of the solution, low nitrogen flow and deposition temperatures close to 100oC. Nevertheless, the substrate position can also influence the crystallinity and amount of deposited material. In summary, we optimized the deposition parameters for the development of thick and high quality films that could be used for the development of sensors in the future.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
tese.pdf (7.18 Mbytes)
Fecha de Publicación
2005-08-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.