Tesis Doctoral
DOI
https://doi.org/10.11606/T.58.2019.tde-27032019-095142
Documento
Autor
Nombre completo
Francine Lorencetti da Silva Campioni
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2018
Director
Tribunal
Corona, Silmara Aparecida Milori (Presidente)
Messias, Danielle Cristine Furtado
Scatolin, Renata Siqueira
Zotti, Fabiana Almeida Curylofo
Título en portugués
Análise da microdureza e morfologia superficial da dentina de dentes decíduos biomodificada com quitosana após indução de lesão de cárie dentária artificial
Palabras clave en portugués
Dentição decídua
Dentina
Odontologia minimamente invasiva
Quitosana
Resumen en portugués
Quitosana é um biopolímero natural obtido a partir da desacetilação de quitina. Embora a quitosana já seja utilizada na Odontologia, seu papel sobre o substrato dentinário de dentes decíduos não está bem elucidado. Portanto, o objetivo do presente estudo foi avaliar o papel da incorporação do gel de quitosana a 2,5 % na dentina de dentes decíduos afetada por lesão de cárie. Dentes decíduos extraídos foram coletados e submetidos à indução de lesão de cárie artificial. Após teste de microdureza inicial (n=28), os dentes foram estratificados para receber gel de quitosana a 2,5%. A superfície dentinária hígida (n=3), dentina desmineralizada (n=3) e dentina biomodificada com gel de quitosana a 2,5% (n=3) foram submetidas à Espectroscopia de Energia Dispersiva de Raio-X (EDS) e Microscopia Eletrônica de Varredura (MEV). O teste de microdureza também foi realizado após a indução de lesão de cárie artificial e após a biomodificação da dentina. Os dados foram avaliados usando o teste paramétrico one-way ANOVA para medidas repetidas. A análise dos dados para EDS foi efetuada por meio de teste não paramétrico de Kruskal-Wallis seguido pelo ajuste dos valores de significância pela correção de Bonferroni para múltiplos testes, bem como por meio de estatística descritiva dos dados obtidos através da fórmula: Variável de estudo controle/ controle × 100. A biomodificação da dentina não alterou a microdureza da superfície dentinária (p=0,339). A porcentagem atômica de cálcio revelou diferenças estatisticamente significantes antre a dentina hígida e biomodificada com quitosana (p<0.022), assim como a porcentagem atômica de fósforo que se mostrou superior no grupo que sofreu a biomodificação. A MEV revelou um expressivo número de túbulos dentinários obliterados, porém com maior diâmetro. As imagens topográficas revelaram, ainda, uma superfície lisa e regular após a biomodificação. Embora a aplicação do gel de quitosana a 2,5% na dentina parcialmente desmineralizada em dentes decíduos não foi capaz de aumentar o valor de microdureza, a biomodificação gerou uma superfície dentinária apropriada para procedimentos restauradores adesivos
Título en inglés
Microhardness and surface morphology dentin analysis in primary teeth biomodified with chitosan after artificial caries lesion induction
Palabras clave en inglés
Chitosan
Dentin
Minimally invasive dentistry
Primary teeth
Resumen en inglés
Chitosan is a natural biopolymer obtained from chitin deacetylation. Although chitosan is already used in dentistry, this role on the primary teeth dentin substrate is not well elucidated. So, the aim to this study was to evaluate the role of the 2.5% chitosan gel incorporation in primary caries-affected dentin teeth. Extracted primary teeth were collected and submitted to artificial caries induction. Teeth were stratified to receive 2.5% chitosan gel after dentin microhardness initial test (n= 28). Healthy dentin (n=3), demineralized dentin (n=3) and biomodified dentin with 2.5% chitosan gel (n=3) were submitted to Energy Dispersive X-ray Spectroscopy (EDS) and Scanning Electron Microscopy (SEM). Microhardness Test was performed too after artificial caries induction and after dentin biomodification. Data were evaluated using one-way ANOVA repeated measures parametric test. Data analysis for EDS was performed using non-parametric Kruskal-Wallis test followed by adjustment of significance values by Bonferroni correction for multiple tests, as well as by means of descriptive statistics of the data obtained using the formula: Study variable control/control × 100. Dentin biomodification did not alter the subsurface microhardness of dentin (p=0,339). The calcium atomic percentage showed statistically significant differences between healthy and biomodificated dentin (p<0.022) and too presented superior phosphorus atomic percentage. SEM revealed expressive number of dentinal tubules obliterated, but a larger diameter. Topographic images revealed a smooth and regular surface in biomodified dentin. Although 2.5% chitosan gel application on partially demineralized dentin in primary teeth was not able to increase microhardness, the biomodification generated an appropriate dentin surface for adhesive restorative procedures
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-07-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.