• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.58.2022.tde-05122022-150816
Documento
Autor
Nombre completo
Stephanie de Oliveira Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2022
Director
Tribunal
Souza, Fernanda de Carvalho Panzeri Pires de (Presidente)
Danelon, Marcelle
Queiroz, Alexandra Mussolino de
Romão, Dayse Andrade
 
Título en portugués
Efeito da adição de vitrocerâmica bioativa em dentifrício sobre abrasividade e remineralização do esmalte dental
Palabras clave en portugués
Biomaterial
Biosilicato
Cárie dentária
Dentifrício
Higiene oral
Lesão de mancha branca
Remineralização dentária
Resumen en portugués
O objetivo deste estudo foi avaliar o efeito da adição de Biosilicato em dentifrício experimental na abrasividade e na remineralização sobre esmalte dental. A ação do dentifrício com 10% de Biosilicato (Bio) foi comparada ao dentifrício convencional (Controle), dentifrício experimental com fluoreto de sódio - 1450ppm (Flúor) e suspensão de Biosilicato a 10%. O dentifrício experimental foi obtido a base de carboximetilcelulose + glicerol + sílica espessante + sílica abrasiva. O Biosilicato foi adicionado ao dentifrício e à água destilada em concentração de 10% em peso. Blocos de esmalte de dentes bovinos (6mm x 6mm x 2mm) foram obtidos e submetidos à análise de microdureza (Microdurômetro HMV, Shimadzu) e rugosidade de superfície (Rugosímetro Surfcorder SE 1700) do esmalte. Os blocos foram submetidos a desafio cariogênico com gel de carboximetil cellulose 8%. Os tratamentos com dentifrícios foram realizados através de escovação simulada (Pepsodent, MAVTEC) por 14.600 ciclos. A suspensão foi aplicada nos espécimes por imersão durante 8h seguido de 16h em saliva artificial a 37ºC por 60 dias, totalizando 1.440 ciclos. Após os tratamentos, leituras finais de microdureza e rugosidade de superfície foram realizadas e imagens em microscopia eletrônica de varredura (MEV) foram realizadas para analisar morfologicamente as amostras após os tratamentos. Os dados foram analisados (One-way ANOVA, Tukey, p<0,05) e demonstraram que a menor alteração de rugosidade de superfície ocorreu após o tratamento com suspensão, diferente estatisticamente (p<0,05) de todos os outros grupos. Bio resultou em microdureza diferente de Flúor (p<0,05). As imagens de MEV demonstraram que os tratamentos com Biosilicato resultaram em superfícies abrasionadas com deposição de vitrocerâmica sobre a superfície. Concluiu-se que Bio resultou em abrasividade semelhante ao Controle e que o Biosilicato pode ser um tratamento eficiente para o tratamento da lesão de mancha branca.
 
Título en inglés
Effect of bioactive glass-ceramic addition on abrasivity of toothpaste and remineralization of dental enamel
Palabras clave en inglés
Biomaterial
Biosilicate
Dental caries
Dental remineralization
Dentifrice
Oral hygiene
White spot lesion
Resumen en inglés
The purpose of this study was to evaluate the effect of the addition of Biosilicate to an experimental toothpaste on the abrasiveness and remineralization of tooth enamel. The action of toothpaste with 10% Biosilicate (Bio) was compared to a conventional toothpaste (Control), experimental toothpaste with sodium fluoride - 1450ppm (Fluoride) and suspension of Biosilicate at 10%. The experimental toothpaste was obtained based on carboxymethylcellulose + glycerol + thickening silica + abrasive silica. The Bio was added on toothpaste and in distilled water in 10% Biosilicate (by weight). Bovine tooth enamel blocks (6mm x 6mm x 2mm) were obtained and submitted to analysis of enamel microhardness (HMV Microhardness Meter, Shimadzu) and surface roughness (Rugometer Surfcorder SE 1700). The fragments were submitted to cariogenic challenge. The toothpaste treatments were performed using simulated toothbrushing (Pepsodent, MAVTEC) for 14,600 cycles. The suspension was applied to the specimens by immersion for 8h followed by 16h in artificial saliva at 37ºC for 60 days, totaling 1,440 cycles. After the treatments, final readings of microhardness and surface roughness were performed, and SEM images were recorded for morphological analysis of the samples after the treatments. Data were analyzed (One-way ANOVA, Tukey, p<0.05) and demonstrated that the smallest change in surface roughness occurred after the suspension treatment, statistically different (p<0.05) from all other groups. Bio resulted in microhardness different from Fluorine (p<0.05). SEM images demonstrated that treatments with Biosilicate resulted in abraded surfaces with deposition of glass-ceramic on the surface. It was concluded that Bio resulted in similar abrasiveness to Control and that Biosilicate can be an efficient treatment for the treatment of white spot lesion.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2022-12-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores.
CeTI-SC/STI
© 2001-2024. Biblioteca Digital de Tesis y Disertaciones de la USP.