Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.58.2020.tde-20092018-134925
Document
Auteur
Nom complet
Tatiana Carvalho Montes
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2018
Directeur
Jury
Regalo, Simone Cecilio Hallak (Président)
Lepri, Cesar Penazzo
Mazzetto, Marcelo Oliveira
Soares, Paulo Vinicius
Titre en portugais
Efeito de solução experimental de quitosana com extratos naturais nas propriedades físicas, morfológicas e adesivas da dentina radicular
Mots-clés en portugais
Dentina radicular
Dessensibilizantes
Erosão dentinária
Hipersensibilidade dentinária
Permeabilidade dentinária
Resumé en portugais
O objetivo do estudo foi analisar as alterações provocadas na permeabilidade e morfologia da dentina radicular, quando tratada com uma solução experimental de quitosana contendo em sua composição os extratos naturais do chá verde (EGCG) e do fruto da planta gardênia (genipin), por meio da mensuração da condutância hidráulica da dentina e morfologia e avaliar seu efeito na resistência de união em restaurações de resina composta, por meio do ensaio de microtração. Os espécimes foram confeccionados a partir da dentina radicular de incisivos bovinos. Para o teste de permeabilidade dentinária e análise em microscopia confocal a laser, foram utilizados 45 discos de dentina, com 4mm de diâmetro e 1mm de espessura, divididos em 3 grupos (n=15): Controle, Dessensibilize Nano P (NP) e solução experimental de quitosana (SE). Foram realizadas 3 mensurações da permeabilidade dentinária: Permeabilidade mínima (presença da smear layer na face externa dos discos de dentina); permeabilidade máxima (remoção da smear layer com ácido cítrico 6%) e a permeabilidade pós-ciclagens/tratamentos (ciclagens erosivas com ácido cítrico 0,3% e tratamentos dessensibilizantes), com análise em microscopia confocal a laser após o desafio erosivo (permeabilidade máxima) e ao término das ciclagens/tratamentos. Posteriormente, foram confeccionados 30 espécimes de 6 x 6mm, divididos nos grupos (n=10) de acordo com o tratamento dessensibilizante (controle - sem tratamento; Dessensibilize Nano P; solução experimental de quitosana) para ensaio de microtração. Foram realizadas as aplicações dos agentes dessensibilizantes na superfície da dentina desmineralizada, após a exposição ao ácido clorídrico (pH 1,2), com posterior confecção de um platô de 4mm de resina composta. Os espécimes restaurados foram cortados em fragmentos de 1mm de largura por 1mm de espessura e levados a máquina de ensaios universais para o teste a uma velocidade de 0,5 mm/minuto, com célula de carga de 500 N. Os padrões de fratura foram analisados em microscópio confocal a laser. As permeabilidades máxima e mínima em relação a pós-ciclagem/tratamentos dentro de cada grupo e entre os grupos, foram analisados pelo teste de Mann-Whitney (α=5%). Para a microtração foi empregado ANOVA e teste de Tukey (α=5%). Os dados foram analisados, quanto ao número, área e perímetro dos túbulos, pelo teste de Kruskal- Wallis (α=5%). Os grupos NP e SE apresentaram diminuição significativa da permeabilidade dentinária para todas as análises, porém no grupo controle houve um aumento da condutância hidráulica. SE não influenciou na resistência de união em resinas compostas, contudo, NP a reduziu significativamente. O maior número de obliterações dos túbulos dentinários foi verificado para o grupo SE. Pode-se concluir que SE promoveu um efeito na diminuição da permeabilidade, obliterando os túbulos dentinários, sem afetar a resistência adesiva.
Titre en anglais
Effect of chitosan experimental solution with natural extracts on physical, morphological and adhesive properties of root dentin
Mots-clés en anglais
Dentin erosion
Dentin hypersensitivity
Dentin permeability
Desensitizers
Root dentin
Resumé en anglais
The aim of this study was to analyze the changes in root dentin permeability and morphology when treated with a chitosan experimental solution containing green tea (EGCG) and gardenia fruit (genipin) naturals extracts, through the dentin hydraulic conductance measurement and morphology and to evaluate its effect on bond strength in composite resin restorations, through the microtensile test. Specimens were made from the root dentin of bovine incisors. For the dentin permeability test and laser confocal microscopy analysis, 45 dentin disks with 4mm diameter and 1mm thickness were used, divided into 3 groups (n = 15): control (C), Dessensibilize Nano P (NP ) and chitosan experimental solution (ES). Three measurements of dentin permeability were performed: Minimum permeability (smear layer presence on the dentin discs outer face); maximum permeability (removal of smear layer with 6% citric acid) and post-cycling permeability/treatments (citric acid 0.3% erosive cycling and desensitizing treatments), with laser confocal microscopy after the erosive challenge (maximum permeability) and at the end of the cycling/treatments. Thereafter, 30 specimens of 6 x 6mm were divided into groups (n = 10) according to the desensitizing treatment (control - without treatment; Desensibilize Nano P; chitosan experimental solution) for microtensile test. The desensitizing agents were applied to the surface of the demineralized dentin after exposure to hydrochloric acid (pH 1.2), thereafter a 4mm plateau of composite resin was made. The restored specimens were cut into 1x1 mm fragments and taken to the universal test machine for testing at a 0.5 mm / min speed with a 500 N load cell. The fracture patterns were analyzed in a confocal laser microscope. Mann-Whitney test (α = 5%) was used for comparisons of maximum and minimum permeability to post-cycling / treatments within each group and between groups. For microtraction, in means comparison between groups, ANOVA 1 criteria with Tukey test (α = 5%) was used. The data obtained from the difference between the final and the initial for dentin tubules number, area and perimeter were submitted to the Kruskal-Wallis test (α = 5%). The NP and ES groups showed a significant decrease in dentin permeability for all analyzes, but in the control group there was an increase in the hydraulic conductance. ES did not influence in dentin bond strength of composite resins, however, NP25 reduced it significantly. The largest number of dentinal tubules obliterations was verified in ES group. It can be concluded that ES decrease dentin permeability, closed dentin tubules without negatively affected the adhesion.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Libération
2021-04-04
Date de Publication
2020-05-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.