Disertación de Maestría
DOI
10.11606/D.58.2018.tde-28022018-135318
Documento
Autor
Nombre completo
Mayara Manfrin Arnez
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2016
Director
Tribunal
Catirse, Alma Blasida Concepcion Elizaur Benitez (Presidente)
Godoi, Ana Paula Terossi de
Reis, Andréa Candido dos
Stuani, Maria Bernadete Sasso
Título en portugués
Rugosidade superficial e microdureza de materiais restauradores provisórios submetidos a ação de enxaguatórios bucais
Palabras clave en portugués
Antissépticos bucais; Cimentos de ionômeros de vidro; Dureza; Materiais dentários
Resumen en portugués
O objetivo deste estudo foi avaliar a rugosidade superficial (µm) e microdureza Vickers (VH) de materiais restauradores temporários: cimento Biodentine™ (M1) e o cimento de ionômero de vidro - Fuji IX (M2) submetidos a diferentes enxaguatórios bucais. Foram confeccionados 54 corpos de prova (cps) por meio de uma matriz de teflon (6mm x 2mm), distribuídos aleatoriamente em 6 grupos de acordo com a solução utilizada: água destilada (S1), enxaguatório com álcool - Listerine Cool Mint (S2) e enxaguatório sem álcool - Colgate Plax (S3). Todos os cps foram mantidos em umidade relativa de 100%, em estufa 37±1°C durante todo o experimento, exceto nos períodos de imersão nos enxaguatórios estabelecidos. Os cps foram colocados individualmente em um frasco contendo 8mL do enxaguatório específico para cada grupo, durante 2 minutos, sob vibração, duas vezes ao dia, por um período de 21 dias. As leituras foram realizdas por meio do microdurômetro e rugosímetro nos tempos de 48 horas (T0), 7 dias (T1), 14 dias (T2) e 21 dias (T3). Os dados obtidos foram agrupados em tabelas e submetidos aos testes estatísticos de normalidade, Kolmogorov-Smirnov, Shapiro-Wilk, Anova e Teste de Tukey por meio do Programa Estatístico Assistat Versão 7.7 beta (2016). Resultados: Verificou-se que os fatores Tempo (T), Solução (S) e Material (M) isoladamente e a interação TxM e SxM tiveram efeito estatisticamente significante na rugosidade superficial. Isoladamente, T3 (0,92±0,02) e M1 (0,87±0,01) apresentaram maior média de rugosidade e S3 (0,72±0,02) a menor média de rugosidade. Nas interações MxT e SXM, respectivamente o M1T3 (1,10±0,03) e M1S1 (1,03±0,03) apresentaram maiores médias de rugosidade. Para a microdureza o fator Material isoladamente, e a interação TxS, TxM e SxM tiveram efeito estatisticamente significante. O M1 (61,2±0,87) apresentou maior microdureza, que M2 (54,4±0,87). Para a interação TxS, a condição S2T2 (54,09±2,61) apresentou menor média de microdureza. Para a interação TxM, o M1 comparado com M2 determinou maior microdureza nos tempos T0, T1 e T2. E para a interação SxM, M1S1 (61,59±1,51) e M1S2 (62,86±1,51) apresentaram maior microdureza que M2S1 (51,53±1,51) e M2S2 (54,34±1,51). De acordo com a metodologia pode-se concluir que: a) o M1 apresentou maior rugosidade superficial nos tempos T1, T2 e T3 e maior microdureza nos tempos T0, T1, e T2 do que o M2 b) O material M1 apresentou maior microdureza independente das soluções.
Título en inglés
Surface roughness and microhardness of provisory restorative materials submitted to mouthwashes
Palabras clave en inglés
Dental materials; Glass ionomer cements; Hardness; Mouthwashes
Resumen en inglés
The aim of this study was to evaluate the surface roughness (µm) and Vickers microhardness of provisory restorative materials: BiodentineTM (M1) and Fuji IX - glass ionomer cement (M2) were submitted to different mouthwashes. Fifty-four specimens were prepared using a Teflon mold (6mm x 2mm), randomly distributed into 6 groups according to the solution used: distilled water (S1), mouthwash containing alcohol -Listerine Cool Mint (S2) and alcohol-free mouthwash - Colgate Plax (S3). During the experiment, all specimens were carried out at a relative humidity of 100% in an oven at 37±1°C, except in the soaking periods in the established mouthwashes. The samples were individually placed in a flask containing 8mL of the specific mouthwash for each group for 1 minute, under vibration twice a day for a period of 21 days. The readings of the variables were carried out at the time of 48 hours (T0), 7 days (T1), 14 days (T2) and 21 days (T3). The obtained data were grouped in tables and submitted to the Normality Tests for Statistical Analysis Kolmogorov-Smirnov, Shapiro-Wilk, Anova and Tukey's Test provided by the Statistical software Assistat Program Version 7.7 beta (2016). Results: It was found that there was a significant effect on surface roughness when considered alone Time (T), Solution (S), Material (M) and the interaction between TxM and SxM. On the other hand, T3 (0.92±0.02) and M1 (0.87±0.01) presented the higher roughness and S3 (0.72±0.02) the lowest average roughness. For the interactions MxT and SxM, M1T3 (1,10±0,03) and M1S1 (1,03±0,03) presented higher roughness averages. To microhardness analysis, the material as a alone factor and the interaction TxS, TxM and SxM had a statistically significant effect. M1 (61.2±0.87) presented a higher microhardness than the M2 (54.4±0.87). For the TxS interaction, S2T2 (54.09 ± 2.61) had a lower microhardness average. To TxM interaction, the M1 compared to M2 determined a higher microhardness at T0, T1 and T2. In interaction SxM, M1S1 (61.59±1.51) and M1S2 (62.8 ±1.51) had a higher microhardness than M2S1 (51.53±1.51) and M2S2 (54.3 ±1,51). According to the methodology, it can be concluded that: a) M1 presented greater surface roughnes at T1, T2 and T3 and higher microhardness at T0, T1, and T2 than M2 b) M1 presented a higher microhardness than M2 for S1 and S2.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-09-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.