Master's Dissertation
DOI
10.11606/D.58.2017.tde-16022016-165315
Document
Author
Full name
Ana Carolina Cabral Roque
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Ribeirão Preto, 2016
Supervisor
Committee
Antunes, Rossana Pereira de Almeida (President)
Gomes, Érica Alves
Souza, Fernanda de Carvalho Panzeri Pires de
Title in Portuguese
Efeito do peróxido de carbamida em diferentes concentrações sobre a rugosidade superficial e brilho de uma cerâmica odontológica
Keywords in Portuguese
Brilho
Cerâmica feldspática
Peróxido de carbamida
Rugosidade superficial
Abstract in Portuguese
O gel de peróxido de carbamida é utilizado em concentrações que variam de 10 a 35%, por períodos de 2 a 8 horas diárias e seu efeito sobre os materiais restauradores ainda não está totalmente elucidado. Assim, o objetivo desse estudo foi avaliar a ação do peróxido de carbamida, 10 e 16%, sobre a rugosidade superficial e o brilho de uma cerâmica odontológica feldspática. Foram confeccionados espécimes (n=10), com a cerâmica IPS d.SIGN , que foram submetidos a protocolos de aplicação de gel de peróxido de carbamida a 10 e 16%, nos tempos de 4 ou 3 horas diárias respectivamente, pelo período de 14 dias. A determinação da rugosidade e da alteração de brilho foi realizada no início do tratamento, após 07 e após 14 dias. A rugosidade superficial foi determinada pelo microscópio, LEXT 3D Measuring Laser Microscope OLS4000, OLYMPUS, e a leitura do brilho foi feita pelo aparelho Micro Gloss. Após a obtenção dos dados, foi realizada a análise TwoWay ANOVA, verificou-se que o resultado obtido foi estatisticamente significante para a variável de rugosidade, tanto para os fatores de variação de tempo (p = 0,004), concentração do peróxido de carbamida (p = 0,007) e para a interação entre ambos (p = 0,013). Foi feito o teste de múltiplas comparações com ajustes de Bonferroni, para análise dos resultados obtidos. Na análise do brilho, para os resultados encontrados, não houve diferença estatisticamente significante. Assim, pode-se concluir que o peróxido de carbamida 10% não provocou alterações significativas na rugosidade da cerâmica, mas o peróxido de carbamida a 16% provocou aumento da rugosidade após o período de 14 dias de aplicação, com médias em torno de 4,0 μm. Conclui-se, então, que as restaurações cerâmicas devem ser protegidas antes da aplicação de agentes clareadores à base de peróxido de carbamida 10 ou 16%.
Title in English
The effect of carbamide peroxide in different concentrations on the surface roughness and gloss using dental ceramics
Keywords in English
Carbamide peroxide
Feldspathic ceramics
Gloss
Surface roughness
Abstract in English
The carbamide peroxide gel is used in concentrations ranging from 10 to 35% for periods from 2 to 8 hours daily and its effect on the restorative material isnt yet fully elucidated. The objective of this study was to evaluate the action of carbamide peroxide, 10 and 16%, on the surface roughness and the gloss of a feldspathic dental ceramics. Specimens were prepared (n = 10), IPS d.SIGN ceramics and submitted to carbamide peroxide gel application protocols 10 and 16% at 4 or 3 hours, respectively, at time 14 days. The determination of roughness and gloss was made at baseline, after 07 and after 14 days. The surface roughness was determined by microscope, 3D Measuring Laser Microscope OLS4000 LEXT, OLYMPUS, and the reading of the gloss was taken by Micro Gloss device. After obtaining the data, the TwoWay ANOVA analysis was performed, it was found that the obtained result was statistically significant roughness variable, both for time-variant factor (p = 0.004), concentration of the carbamide peroxide (p = 0.007) and the interaction between both (p = 0.013). It was made for multiple comparisons test with Bonferroni adjustments, for analysis of the results.There was no statistically significant difference in gloss. Thus, it can be concluded that the carbamide peroxide 10% did not cause significant changes in roughness ceramic, but the carbamide peroxide at 16% caused an increased roughness after 14 days of application, averaging around 4, 0 micrometers. Therefore, the ceramic restorations must be protected before the application of bleaching agents based on carbamide peroxide 10 or 16%.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-08-10
 
WARNING: The material described below relates to works resulting from this thesis or dissertation. The contents of these works are the author's responsibility.
  • Painel Científico: (3 . lugar): Análise fotoelástica das tensões geradas por diferentes planejamentos de próteses parciais fixas cimentadas sobre iplantes cone morse - ABROSS 2010 - IX ENCONTRO INTERNACIONAL DA ACADEMIA BRASILEIRA DE OSSEOINTEGRAÇÃO
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.