Master's Dissertation
DOI
10.11606/D.58.2017.tde-15032016-162731
Document
Author
Full name
Glenda Lara Lopes Vasconcelos
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Ribeirão Preto, 2015
Supervisor
Committee
Souza, Valéria Oliveira Pagnano de (President)
Davi, Letícia Resende
Paranhos, Helena de Freitas Oliveira
Title in Portuguese
Efeito das pastilhas higienizadoras efervescentes à base de peróxido alcalino em liga metálica de cobalto-cromo
Keywords in Portuguese
Higienizadores para próteses
Liberação de íons e microscopia eletrônica de varredura
metal
Peróxidos alcalinos
Rugosidade superficial
Abstract in Portuguese
A higienização das próteses é de fundamental importância para a longevidade do tratamento reabilitador. Entretanto, é necessário analisar os efeitos que os higienizadores podem causar nas superfícies que compõem uma prótese. Deste modo, o objetivo deste estudo foi avaliar os efeitos de pastilhas efervescentes à base de peróxido alcalino em liga de cobalto cromo (Co-Cr), utilizada em Prótese Parcial Removível (PPR). A partir de uma matriz metálica, padrões de cera em forma de disco (12 mm x 3 mm) foram confeccionados para posterior fundição. Os espécimes metálicos (n=16) foram imersos nas soluções: água deionizada (controle), Polident 3 minutes®, Steradent®, Efferdent®, Polident for Partials® e Corega Tabs®. Foi realizada a análise da rugosidade (n=10) por meio de rugosímetro, antes (t0) e após 5 períodos de simulação de ½, 1, 2, 3, 4 e 5 anos de imersão nos higienizadores. Foram realizadas análises complementares quantitativas da liberação de íons (n=5) de cobalto (Co), cromo (Cr) e molibdênio (Mo) em cada solução e análises qualitativas em um espécime de cada grupo, por meio de Microscopia Eletrônica de Varredura (MEV) e Espectrometria de Energia Dispersiva de Raios X (EDS). A distribuição dos dados de rugosidade (μm) apresentou-se não normal. Foi utilizada estatística não-paramétrica (α=0,05). Tanto para o fator solução (Kruskall Wallis, ½ ano (p=0,900), 1 ano (p=0,277), 2 anos (p=0,227), 3 anos (p=0,086), 4 anos (p=0,657) e 5 anos (p=0,856), como para o fator tempo (Friedman, p=0,137) não houve diferença significante. Com relação à liberação de íons (μg/L), a distribuição dos dados apresentou-se normal. De acordo com a estatística (α=0,05, ANOVA e teste de Tukey), Corega Tabs®, Efferdent® e água deionizada promoveram maior liberação de íons Co do que o Steradent® (p=0,003). Quanto aos íons Cr (p=0,000), Corega Tabs® propiciou maior liberação quando comparado a água deionizada, Steradent® e Polident 3 minutes®. Em relação aos íons Mo (p=0,001), o Efferdent® promoveu maior liberação. No MEV pode-se verificar que as soluções não apresentaram efeitos deletérios sobre as superfícies. Conclui-se que todas as pastilhas avaliadas não ocasionaram danos, entretanto, Steradent® foi a que propiciou menor liberação de íons, sendo indicada com maior segurança para higienização de superfícies metálicas de PPR.
Title in English
Effect of alkaline peroxide-effervescent tablets on the surfaces of the cobalt-chromium alloys
Keywords in English
Alkaline peroxide
Cobalt-chromium alloy
Denture cleanser
Ions release
Scanning electron microscopy
Surface roughness
Abstract in English
The hygiene care of the removable dentures is of most importance for the longevity of the rehabilitation treatment. However, it is necessary to analyze the effects that denture cleansers can cause on the surfaces of prosthesis. Thus, the aim of this study was to evaluate the effect of alkaline peroxide-effervescent tablets on the surfaces of the cobalt-chromium alloys (Co-Cr), used in removable partial dentures (RPD). Circular specimens (12 mm x 3 mm) were fabricated with cobalt-chromium alloys. The specimens (n= 16) were immersed in the following solutions: deionized water (control), Polident 3 minutes™, Steradent™, Efferdent™, Polident for Partials™ and Corega Tabs™. The surface roughness (n=10) was analyzed with a surf-test analyzer, before and after 5 periods that corresponds to the simulation of ½, 1, 2, 3, 4 and 5 years of immersion in the cleansers. As complementary analysis, it was performed a quantitative study of ions release (n=5) for cobalt (Co), chromium (Cr) and molybdenum (Mo) in each solution and qualitative analysis with scanning electron microscopy (SEM) associated to Energy-dispersive X-ray spectroscopy (EDS). The results of surface roughness had presented no normal. In nonparametric statistics (α = 0.05), both of the solution factor Kruskall Wallis, ½ year (p=0.900), 1 year (p=0.277), 2 years (p=0.227), 3 years (p=0.086), 4 years (p=0.657) and 5 years (p=0.856), such as time factor (Friedman, p = 0.137), there was no significant difference. The results of ionic release presented a normal distribution and they were submitted to ANOVA (p=0.05) and Tukey test. The solutions Corega Tabs®, Efferdent® and deionized water presented greater Co ionic release than Steradent® (p=0.003). For Cr ions (p=0.000), Corega Tabs® had greater ionic release than deionized water, Steradent® and Polident 3 minutes®. Regarding Mo ions (p=0.001), Efferdent® showed greater release. With SEM, it was possible to verify that the solutions showed no deleterious effects on the specimen surfaces. It was concluded that no deleterious effects on metal surface was caused, however, Steradent® presented the smallest ionic release, and can be indicated more safely for cleaning metal surfaces of RPD.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-08-09
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.