Tesis Doctoral
DOI
10.11606/T.58.2002.tde-13112003-101112
Documento
Autor
Nombre completo
Celso de Barros
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2002
Director
Tribunal
Bezzon, Osvaldo Luiz (Presidente)
Araujo, Carlos dos Reis Pereira de
Goes, Mario Fernando de
Orsi, Iara Augusta
Rollo, Joao Manuel Domingos de Almeida
Título en portugués
"Estudo da relação entre resistência à abrasão e dureza de ligas odontológicas de metais básicos para restauração metalocerâmica"
Palabras clave en portugués
Abrasão
Dureza.
Ligas Odontológicas
Resumen en portugués
Embora haja grande exigência por restaurações estéticas livres de metal, restaurações metalocerâmicas, cujas subestruturas feitas com ligas de metais básicos, são procedimentos de rotina nos planejamentos restauradores protéticos. No entanto, a alta resistência ao desgaste destas ligas, caracterizada pela grande dificuldade de acabamento e polimento, tem sido associada à dureza, geralmente elevada. A proposta deste estudo foi avaliar resistência à abrasão e dureza de seis ligas de metais básicos (4 ligas de Ni-Cr, 1 liga de Co-Cr e 1 Ti comercialmente puro – 99,5% Ti) disponíveis comercialmente para uso com cerâmica. A resistência à abrasão foi determinada pela perda de peso dos corpos-de-prova, ao longo de 4 séries de ciclos de abrasão. A dureza Rockwell 30N também foi avaliada nos mesmos intervalos. Os dados foram analisados com o nível de significância a = 0,05. O teste de regressão e correlação da resistência à abrasão e dureza mostrou que para 3 ligas de Ni-Cr (Vera Bond, Vera Bond II e Wiron 99) a linha de regressão foi descendente, indicando que um aumento na dureza correspondeu a uma redução nos valores de perda de peso, enquanto para 1 liga de Ni-Cr (Neochrom) a linha de regressão foi ascendente, indicando um aumento nos valores de perda de peso, apesar de um aumento na dureza. Por outro lado, para a ligas de Co-Cr (New Ceram) e de titânio (Rematitan), os valores de perda de peso se mantiveram constantes. As ligas avaliadas tiveram baixos coeficientes de correlação entre resistência à abrasão e dureza. A análise metalográfica revelou particularidades que podem ter sido determinantes para as taxas de desgaste de cada material. Com exceção da liga de titânio, não houve mudanças metalográficas das ligas avaliadas, durante as séries de ciclos de abrasão.
Título en inglés
Study of relationship between abrasion resistance and hardness of dental base metal alloys for metal ceramic restoration.
Palabras clave en inglés
Abrasion
Dental Alloys
Hardness.
Resumen en inglés
In spite of the demand for metal free restorations, metal ceramic restorations using base metal alloys are routine in prosthodontics. Nevertheless, the high abrasion resistance of base metal alloys, characterized by difficulty in finishing and polishing, has been related to excessive hardness. The purpose of this study was to evaluate abrasion resistance and hardness of six base metal alloys (4 Ni-Cr alloys, 1 Co-Cr alloy and 1 commercially pure Ti alloy – 99.5% Ti) available commercially for use with fused porcelain. Abrasion resistance was determined by specimen weight loss along 4 series of abrasion cycles. The Rockwell 30N hardness was also determined in the same periods. Data were analyzed statistically with the level of significance set at a = 0.05. Regression and correlation analysis of abrasion resistance and hardness showed that for three Ni-Cr alloys (Vera Bond, Vera Bond II and Wiron 99) the regression lines descended indicating that an increase in hardness corresponded to a reduction in weight loss, whereas for one Ni-Cr alloy (Neochrom) the regression line ascended indicating an increase in weight loss in spite of an increase in hardness. On the other hand, for the Co-Cr alloy (New Ceram) and Ti (Rematitan), the weight loss remained constant. The alloys tested had low correlation coefficients between abrasion resistance and hardness. Microscopic analysis showed details that may have been determining for the weight loss rate of each material. With the exception of the titanium alloy, there were no metallographic changes of the alloys tested during the abrasion tests.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
03-Proposicao.pdf (5.19 Kbytes)
04-Material_Metodo.pdf (105.61 Kbytes)
05-Resultados.pdf (229.13 Kbytes)
06-Discussao.pdf (24.42 Kbytes)
07-Conclusoes.pdf (5.77 Kbytes)
Fecha de Publicación
2004-01-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.