Tesis Doctoral
DOI
Documento
Autor
Nombre completo
Alfredo Jorge
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1991
Director
Tribunal
Ferreira, Guilherme Fontes Leal (Presidente)
Alfaro, Renê Armando Moreno
Basso, Heitor Cury
Campos, Milton Soares de
Eiras, José Antonio
Título en portugués
Medidas elétricas no policarbonato durolon e o metododa temperatura oscilante.
Palabras clave en portugués
Medidas elétricas
Policarbonato
Temperatura oscilante
Resumen en portugués
Nesta tese procuramos caracterizar o Policarbonato Bisfenol-A, Durolon® sob o ponto de vista elétrico, separando a reação dipolar e os processos de condução. Apesar de preparadas de forma análoga, as amostras (≅ 30μm de espessura) mostraram comportamento pouco reprodutível, principalmente da componente condutiva. Várias anomalias foram detectadas embora não estudadas em detalhe pela pobre reprodutibilidade já mencionada. Além das técnicas usuais de polarização e despolarização isotérmicas, despolarização termoestimulada e de polarização termoestimulada, empregou-se pela primeira vez, em medidas desta natureza, a técnica de oscilação senoidal da temperatura, estando o campo elétrico aplicado. Media-se a corrente daí decorrente, procurando-se trabalhar sempre com uma mesma amostra. Na região de 50°C a 70°C, diferenças de fase superiores a 90° foram encontradas (o sinal de corrente atrasado em relação ao de temperatura). Uma análise simples destes resultados indica que, neste caso, tanto a condutividade como a suscetibilidade diminuem com o crescimento da temperatura (dX/dT≅ -1x10-3/°C). Medidas de polarização termoestimulada, também, mostram uma inversão da corrente em relação ao campo aplicado desde cerca da temperatura ambiente ate ≅ 90°C. Um estudo sistemático da condução a 120°C indica que portadores são emitidos do eletródio, e que o trânsito dos mesmos é rápido (menor do que o tempo em que a polarização se estabelece, ≅ 2 min). Tensões e correntes espontâneas foram detectadas mesmo em amostras providas de eletródios de mesmo metal (uma correlação com a ordem empregada na metalização foi suspeitada, seguindo observação anteriormente feita pelo Prof. B. Gross). Algumas medidas com eletródios Al-Al, Al-Au e Au-Au foram feitas. Finalmente, sugestões para trabalhos futuros são feitas.
Título en inglés
Electrical measurements in the durolon polycarbonate and method of swing temperature.
Palabras clave en inglés
Electrical measurements
Polycarbonate
Swing temperature
Resumen en inglés
In this work the electrical characterization of the Polycarbonate Bisphenol-A, Durolon ® was attempted, trying to separate the dipole and the conduction processes. However, poor reproducibility, mainly in the conductivity, was achieved even for samples (≅ 30μm thick usually) taken from the same batch. Anomalies were detected but not studied in detail owing the poor reproducibility referred above. Beside the usual techniques like the isothermal polarization and depolarization in short-circuit, thermally depolarization currents and thermally stimulated polarization, in a new one, employed by the first time for the study of transport and polarization, the temperature was oscillated and the ensuing current oscillation was monitored. Large phase shifts (the current lagging the temperature oscillation), even greater ≅ 90° were found in the range 50°C 70°C. A simple analysis indicates that in this case both the conductivity as well as the susceptibility are decreased for increasing temperature (dX/dT≅ -1x10-3/°C). Accordingly thermally stimulated polarization shows a current reversal with respect to the electric field from room temperature to ≅ 90°C. A systematic study of the conduction process at 120°C was carried out, the analysis of which indicates that carriers are emitted from the electrode, whose transit across the sample is shorter than the duration of the polarization current (≅ 2 min). Spontaneous tensions and currents were detected even for samples provisioned with similar electrodes (a correlation with the actual sequence of metallization, following a suggestion by Prof. B. Gross, was surmised). A few measurements with Al-Al, Al-Au and Au-Au electrodes were carried out. Finally suggestions for future work are given.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AlfredoJorgeD.pdf (4.84 Mbytes)
Fecha de Publicación
2009-08-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.