• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
10.11606/D.54.1980.tde-16092010-191916
Document
Auteur
Nom complet
José de Anchieta Rodrigues
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1980
Directeur
Titre en portugais
Propriedades de tração do Nb policristalino dopado com hidrogênio
Mots-clés en portugais
Dutilidade
Encruamento
Hidrogênio
Niobio
Propriedades mecânicas
Resistência mecânica
Soluto intersticial
Taxa de deformação
Tração
Resumé en portugais
Foi estudado, através de ensaio de tração, o Nb policristalino com teor de hidrogênio de 0 a 50 partes por milhão em peso (ppm-p) nas temperaturas de 223, 273 e 293 K. Os ensaios de tração a velocidades constantes foram realizados com taxas iniciais de deformaçao de 4,2 X 10-5 e 42 X 10-5 s-1 , e os parâmetros de ductilidade e resistência mecânica foram analisados em função da concentração de hidrogênio. Foram também obtidos o coeficiente de sensitividade a taxa de deformação (m) e o volume de ativação (V) através de ensaios de tração, alternando-se abruptamente a taxa de deformação entre os valores acima mencionados, em sucessivos pontos da curva tensão-deformação. Para o cálculo destes dois últimos parâmetros foi proposta uma análise detalhada, considerando-se os efeitos elásticos e o encruamento durante a deformação plástica uniforme. Todo o estudo foi acompanhado por análise fratográfica Que permitiu verificar três comportamentos de ruptura da liga Nb-H, dependendo do teor de hidrogênio e da temperatura. A 223K foi observado que há uma forte redução de ductilidade do Nb para teores de hidrogênio até 10 ppm-p, sendo que para este teor o seu comportamento foi totalmente frágil
Titre en anglais
Tensile properties of polycristalline Nb dopped with hydrogen
Mots-clés en anglais
Ductility
Hydrogen
Interstitial solute
Mechanical properties
Mechanical strenght
Niobium
Strain rate
Tensile
Work hardening
Resumé en anglais
Tensile testing at 223, 273 and 293 K was carried out on polycrystalline Nb dopped from 0 to 50 parts per million in weight (ppm-wt) of Hydrogen. The tensile testing at constant velocity was done at 4,2 X 10 -5 and 42 X 10-5 s-1 of initial strain rate, and the ductility and strength parameters was analysed as a function of the hydrogen content. It was also obtained the strain rate sensitivity (m) and the activation volume (V), from tensile testing, cycling between the two above specified strain rates, at several points of the stress-strain curve. For the calculation of this two last parameters it was proposed a detailed analysis, considering the elastic effect and the work hardening during the uniform plastic deformation. All these studies was followed by fratographic analysis that alowed the identification of three rupture behavior for the Nb-H alloy, depending of the temperature and the hydrogen content. At 223 K, it was observed that there is a strong embrittlement of Nb for hydrogen content up to 10 ppm-wt, and for this value the behavior was completely brittle
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2010-09-17
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.