Disertación de Maestría
DOI
10.11606/D.54.1978.tde-16032015-105640
Documento
Autor
Nombre completo
Edgar Dutra Zanotto
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1978
Director
Tribunal
Mascarenhas, Yvonne Primerano
Qualifik, Paul
Título en portugués
Separação de fases amorfas e nucleação de cristais em vidros do sistema Li2O-Si02
Palabras clave en portugués
Não disponível
Resumen en portugués
Foram estudados vidros do sistema Li2O - SiO2, com 29,0 31,0 e 33,3% mol de Li2O, em regiões adjacentes à fronteira de imiscibilidade metaestável. Amostras foram obtidas por meio da técnica de splat cooling. Caracterizou-se o desenvolvimento da separação de fases amorfas com o tratamento térmico, através da evolução da intensidade integrada do espalhamento de raios-X a baixos ângulos. Utilizando-se de microscopia ótica de reflexão e métodos estereológicos, definiu-se a cinética de nucleação de cristais, mostrando-se de maneira clara que a separação de fases acelera a nucleação cristalina em vidros desse sistema. Observou-se também, que esse efeito é mais acentuado durante o estágio de nucleação e crescimento da separação amorfa que na etapa de coarsening. Os resultados obtidos experimentalmente, sugerem que o gradiente de concentração existente na vizinhança das partículas vítreas separadas, contribui apreciavelmente à aceleração da nucleação de cristais. Um aumento significativo da mobilidade atômica, através das interfaces das fases amorfas, poderia ser uma explicação alternativa ou complementar para o efeito verificado. Adicionalmente, mostrou-se as razões pelas quais vários autores concluíram que a separação amorfa não influencia a nucleação cristalina
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
Phase separation and its influence on crystal nucleation in Li2O - SiO2 glasses were studied. Samples having 29,0%, 31,0% and 33,3% mol Li2O were obtained by the splat cooling technique. The development of amorphous phase separation with heat treatment was characterized by determining the evolution of the integrated intensity of small angle x-rays scattering. Using the optical reflection microscopy and stereological techniques, the kinetics of crystal nucleation was defined, and it was proved that phase separation accelerates crystal nucleation in glasses belonging to this system. It was also observed that this effect is more pronounced during the nucleation and growth stage of amorphous separation than during the coarsening stage. The experimental results suggest that the depleted zone around the separated vitreous particles plays an important role on the acceleration of crystal nucleation. The increase in atomic mobility through the interfaces of the amorphous phases could be an alternative or complementary explanation to the observed effect. Additionally, arguments were given to explain why several authors found that that amorphous separation does not influence crystal nucleation
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-03-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.