Disertación de Maestría
DOI
10.11606/D.54.1984.tde-14102009-093531
Documento
Autor
Nombre completo
Osvaldo Novais de Oliveira Junior
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1984
Director
Título en portugués
Estudo do transporte de carga em amostras de teflon FEP sob descarga corona no ar e no nitrogênio.
Palabras clave en portugués
Descarga corona
Polímeros
Resumen en portugués
O Triodo de corona com corrente constante foi utilizado em medidas da evolução do potencial de superfície de amostras de FEP 12 e 25 μm, carregadas com corona positiva e negativa no FEP 12 e 25 μm carregadas com corona positiva e negativa no ar e no nitrogênio. Estas medidas permitem concluir que não há diferença a nível de transporte de cargas entre os resultados com os dois gases. Apenas a umidade é importante para a subida e o decaimento do potencial de superfície. A subida do potencial de superfície de amostras de FEP 12 μm carregadas com corona negativa foi interpretada por meio da justaposição de dois modelos teóricos. No material só existem armadilhas profundas, em número finito, tanto na superfície quanto no volume; sendo que as de volume estão uniformemente distribuídas. Nenhum decaimento significativo de potencial é observado. A superfície desempenha um papel predominante na captura e injeção de portadores nas amostras de 12 μm carrega - das com corona positiva. Um modelo teórico que supõe schubweg dependente do campo médio reproduz os resultados experimentais.
Título en inglés
Charge transport in FEP Teflon Films submsted to corona discharge in air and in nitrogen.
Palabras clave en inglés
Corona discharge
Polymer
Resumen en inglés
The corona triode with constant current was used to measure the evolution of surface potential of FEP 12 and 25 μm samples, charged with positive and negative corona in air and in nitrogen. No difference in the transport properties in thin samples was observed when the gas was changed and this allowed us to conclude that electrons and holes are the carriers responsible by the transport of charge in the material. Only the moisture is important to the build up and decay of surface potential. The build up of surface potential of 12 μm samples charged with negative corona was interpreted by means of a deep fast trapping model in the beginning, followed by an increase of the trapping time when saturation is approached. Surface traps are also present. No significative potential decay is observed. The surface performs an important role in the trap¬ ping and injection of carriers into the bulk of 12 μm samples charged with positive corona. A theoretical model that assumes schubweg dependent on mean electric field fits the experimental results.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-10-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.