Tese de Doutorado
DOI
10.11606/T.54.1988.tde-13102014-152807
Documento
Autor
Nome completo
Elisabeth Pavão de Castro
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1988
Orientador
Banca examinadora
Camargo, Paulo Cesar de (Presidente)
Eiras, José Antonio
Jordao, Jose Alberto Rodrigues
Li, Maximo Siu
Terrile, Maria Cristina
Título em português
Estudo das interações magneto-elásticas em ligas de cromo-vanádio
Palavras-chave em português
Ligas cromo-vanadio; Interações magnetoelasticas; Ultrassom; Antiferomagnetismo itinerante
Resumo em português
Medidas de atenuação ultrassônica e constante elástica em ligas de Cr-V, utilizando técnicas de pulso eco foram realizadas e as transições na temperatura de Neel, TN, estudadas. Um modelo teórico é proposto para descrever os comportamentos da atenuação e constante elástica perto da transição em TN. De acordo com o modelo proposto a adição de vanádio diminui drasticamente o coeficiente de difusão, modificando a natureza da transição. Foram utilizadas amostras de cromo contendo 0,2%V; 0,5%V; 0,67%V; 1,0%V e 1,5%V. A partir da dependência aproximadamente linear de TN com a concentração de vanádio conclui-se que 3,3% V corresponderá à TN= 0K. O efeito do campo magnético até 4,5T revelou-se insuficientemente para a obtenção de monodomínio magnético e não causa nenhuma variação mensurável em TN
Título em inglês
Study of magnetoelastic interactions on chromium-vanadium alloys
Palavras-chave em inglês
Chromium-vanadium alloys; Magneto-elastic interactions; Itinerant antiferromagnetism; Ultrasound
Resumo em inglês
Measurements of ultrasonic attenuation and elastic Constant in Cr-V alloys, using pulse echo techniques were realized and the transitions at the Neel temperature, TN, were studied. We propose a theoretical model which describe the behavior of the ultrasonic attenuation and elastic Constant near the transition in TN. According to the theoretical model the addition of Vanadium to chromium, drastically diminishes the diffusion coefficient thus changing the nature of the transition. It was used samples of chromium containing 0,2%V; 0,5%V; 0,67%V; 1,0%V and 1,5%V. From the approximately linear dependence of TN with the vanadium concentration it was concluded that 3,3%V corresponds to TN= 0. The effect of magnetic fields up to 4,5T was insufficient to produce single-Q samples, and did not cause any mensurable variation in TN
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2014-10-20
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.