Thèse de Doctorat
DOI
10.11606/T.54.1988.tde-13102014-152807
Document
Auteur
Nom complet
Elisabeth Pavão de Castro
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1988
Directeur
Jury
Camargo, Paulo Cesar de (Président)
Eiras, José Antonio
Jordao, Jose Alberto Rodrigues
Li, Maximo Siu
Terrile, Maria Cristina
Titre en portugais
Estudo das interações magneto-elásticas em ligas de cromo-vanádio
Mots-clés en portugais
Ligas cromo-vanadio; Interações magnetoelasticas; Ultrassom; Antiferomagnetismo itinerante
Resumé en portugais
Medidas de atenuação ultrassônica e constante elástica em ligas de Cr-V, utilizando técnicas de pulso eco foram realizadas e as transições na temperatura de Neel, TN, estudadas. Um modelo teórico é proposto para descrever os comportamentos da atenuação e constante elástica perto da transição em TN. De acordo com o modelo proposto a adição de vanádio diminui drasticamente o coeficiente de difusão, modificando a natureza da transição. Foram utilizadas amostras de cromo contendo 0,2%V; 0,5%V; 0,67%V; 1,0%V e 1,5%V. A partir da dependência aproximadamente linear de TN com a concentração de vanádio conclui-se que 3,3% V corresponderá à TN= 0K. O efeito do campo magnético até 4,5T revelou-se insuficientemente para a obtenção de monodomínio magnético e não causa nenhuma variação mensurável em TN
Titre en anglais
Study of magnetoelastic interactions on chromium-vanadium alloys
Mots-clés en anglais
Chromium-vanadium alloys; Magneto-elastic interactions; Itinerant antiferromagnetism; Ultrasound
Resumé en anglais
Measurements of ultrasonic attenuation and elastic Constant in Cr-V alloys, using pulse echo techniques were realized and the transitions at the Neel temperature, TN, were studied. We propose a theoretical model which describe the behavior of the ultrasonic attenuation and elastic Constant near the transition in TN. According to the theoretical model the addition of Vanadium to chromium, drastically diminishes the diffusion coefficient thus changing the nature of the transition. It was used samples of chromium containing 0,2%V; 0,5%V; 0,67%V; 1,0%V and 1,5%V. From the approximately linear dependence of TN with the vanadium concentration it was concluded that 3,3%V corresponds to TN= 0. The effect of magnetic fields up to 4,5T was insufficient to produce single-Q samples, and did not cause any mensurable variation in TN
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-10-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.