Tesis Doctoral
DOI
10.11606/T.54.1988.tde-13102014-152807
Documento
Autor
Nombre completo
Elisabeth Pavão de Castro
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1988
Director
Tribunal
Camargo, Paulo Cesar de (Presidente)
Eiras, José Antonio
Jordao, Jose Alberto Rodrigues
Li, Maximo Siu
Terrile, Maria Cristina
Título en portugués
Estudo das interações magneto-elásticas em ligas de cromo-vanádio
Palabras clave en portugués
Ligas cromo-vanadio; Interações magnetoelasticas; Ultrassom; Antiferomagnetismo itinerante
Resumen en portugués
Medidas de atenuação ultrassônica e constante elástica em ligas de Cr-V, utilizando técnicas de pulso eco foram realizadas e as transições na temperatura de Neel, TN, estudadas. Um modelo teórico é proposto para descrever os comportamentos da atenuação e constante elástica perto da transição em TN. De acordo com o modelo proposto a adição de vanádio diminui drasticamente o coeficiente de difusão, modificando a natureza da transição. Foram utilizadas amostras de cromo contendo 0,2%V; 0,5%V; 0,67%V; 1,0%V e 1,5%V. A partir da dependência aproximadamente linear de TN com a concentração de vanádio conclui-se que 3,3% V corresponderá à TN= 0K. O efeito do campo magnético até 4,5T revelou-se insuficientemente para a obtenção de monodomínio magnético e não causa nenhuma variação mensurável em TN
Título en inglés
Study of magnetoelastic interactions on chromium-vanadium alloys
Palabras clave en inglés
Chromium-vanadium alloys; Magneto-elastic interactions; Itinerant antiferromagnetism; Ultrasound
Resumen en inglés
Measurements of ultrasonic attenuation and elastic Constant in Cr-V alloys, using pulse echo techniques were realized and the transitions at the Neel temperature, TN, were studied. We propose a theoretical model which describe the behavior of the ultrasonic attenuation and elastic Constant near the transition in TN. According to the theoretical model the addition of Vanadium to chromium, drastically diminishes the diffusion coefficient thus changing the nature of the transition. It was used samples of chromium containing 0,2%V; 0,5%V; 0,67%V; 1,0%V and 1,5%V. From the approximately linear dependence of TN with the vanadium concentration it was concluded that 3,3%V corresponds to TN= 0. The effect of magnetic fields up to 4,5T was insufficient to produce single-Q samples, and did not cause any mensurable variation in TN
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-10-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.