Thèse de Doctorat
DOI
10.11606/T.54.1991.tde-02042015-151449
Document
Auteur
Nom complet
Guillermo Guzman Martel
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1991
Directeur
Jury
Aegerter, Michel Andre (Président)
Andreeta, Jose Pedro
Campos, Milton Soares de
Casarini, Jose Roberto
Souza, Dulcina Maria Pinatti Ferreira de
Titre en portugais
Síntese e caracterização de cerâmicas ferroelétricas Pb (Mg1Nb2/3)O3
Mots-clés en portugais
Não disponível
Resumé en portugais
Neste trabalho foram estudadas as propriedades dielétricas do relaxador ferroelétrico Pb (Mg1Nb2/3)O3. O pó PMN puro foi preparado por métodos clássicos (moagem e calcinação) e por coprecipitação em solução aquosa. A reatividade do magnésio, que influi no aparecimento da fase pirocloro deletérea Pb3Nb4O13, foi estudada usando óxidos , carbonatos e nitratos. A reatividade do Chumbo também foi estudada usando as duas formas halotrópicas do PbO. Foi observada a influência da distribuição do tamanho de partículas dos óxidos de chumbo e de nióbio na formação do PMN. O PMN quase-puro foi preparado com o uso de nitrato de magnésio, óxido de chumbo tipo ortorrômbico e óxido de nióbio, estes dois últimos, com tamanho médio de partículas de 2,5μm e 1μm respectivamente. A sinterização do PMN foi realizada a 950°C durante 4h. Aditivos tais como 4% PbO e 2%MgO são fundamentais para se obter cerâmicas PMN com densidade aparente þ > 0,9 þ teórico. Estudou-se também a dependência da constante dielétrica em função da proporção de fase perovskita, da densidade aparente e do tamanho de grão e para amostras contendo 100% PMN, esta dependência pode ser descrita qualitativamente pelo modelo de Looyenga. Com base neste modelo, a otimização das propriedades deilétricas do PMN deveriam ser obtidas para cerâmicas contendo 100% de fase perovskita, densidade aparente e do tamanho de grão da ordem de 5 a 8μm.
Titre en anglais
Not available
Mots-clés en anglais
Not available
Resumé en anglais
In this work we have studied the synthesis of the ferroelectric relaxor Pb (Mg1Nb2/3)O3 (called PMN), its dielectric properties 9K(t, ν) and tanδ (T, ν) and their dependences with the apparent density and grain size. PMN powders have been prepared by classical method (milling and calcination of precursors) and by coprecipitation method in aqueous solution. The reactivity of the magnesium, which strongly influences the formation of the magnesium, which strongly influences the formation of a deleterious pyrochlore phase (Pb3Nb4O13), has been studied using oxide, carbonates and nitrates; the reactivity of lead has been determined for the two allotropic forms: PbO red and yellow. Concentration of PMN phase higher than 96% has been best obtained with the use of magnesium nitrate, orthorrombic lead oxide and niobium oxide, the mean particle size of the last two compounds being ,5μm and 1μm respectively. The PMN ceramics have been sintered at 950°C during 4h. However, addition of 4 wt% PbO and 2 wt% MgO were found fundamental to obtain a 100% PMn ceramics with apparent density þ > 0,9 þ th. The original synthesis pf PMN by coprecipitation I aqueous solution allowed the preparation of a 100% PMN powder; the occurrence of the parasitic pyrochlore phase was never observed during the various steps of the process. The dielectric properties (K and tanδ) have been studied as a function of the frequency an temperature. Dielectric constant Kmax = 17200 and 15400 at the Curie temperature (T ± 10°C) have been measured for sintered ceramics obtained with powders prepared classically and by coprecipitation respectively. The dependence of the dielectric constant on the percentage of the perovskite phase (PMN), the apparent density ρ and the grain size d, for ceramics containing 100% PMN, was shown to follow qualitatively, the Looyengas model. Consistent with this model, it was found that the optimum dielectric properties were attained for ceramics having 100% PMN perovskite phase, apparent density close to the theoretical density, and grain size between 5 to 8μm
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-04-07
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.