Disertación de Maestría
DOI
10.11606/D.54.1990.tde-02042015-120328
Documento
Autor
Nombre completo
Eduardo Colla Ruvolo Junior
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1990
Director
Tribunal
Aegerter, Michel Andre (Presidente)
Andreeta, Jose Pedro
Zanotto, Edgar Dutra
Título en portugués
Preparação e caracterização de sílica amorfa ultrapura pelo processo sol-gel.
Palabras clave en portugués
Não disponível
Resumen en portugués
A preparação de materiais vítreos e cerâmicos pelo processo sol-gel vem ganhando um desenvolvimento muito grande nos últimos anos, superando em muitos casos as tecnologias convencionais. Este trabalho apresenta um processo sol-gel original de modo a obter sílica densa, amorfa e monolítica cuja estrutura gel é reforçada mecanicamente pela adição ao sol inicial de microesferas de sílica preparadas pelo método de Stöber ou pó de sílica comercial (Cab-O-Sil M5), evitando o problema de quebras. Análises feitas com microscopia eletrônica de transmissão (TEM), área superficial BET, tempo de gelificação, difratometria de raio-x, densidade, microdureza Vickers, espectroscopia de absorção óptica do ultravioleta ao infravermelho caracterizam cada uma das etapas das transições sol-gel úmido-gel seco-vidro. Os materiais vítreos preparados apresentam qualidade óptica comparável à da sílica comercial
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
The preparation of glasses and ceramics by the sol-gel process received notable development in the last few years, showing in many cases great advantages on conventional technologies. This work presents an original sol-gel process in order to obtain dense, amorphous and monolithic-silica whose gel structure is reinforced mechanically by addition to the initial sol of either silica microspheres prepared by the Stöber method or fumed silica powder (Cab-O-Sil M5 Cabot), avoiding the cracks problem. Analysis of transmission electron microscopy (TEM), BET surface area, gelation time, x-ray difratometry, density, Vickers microhardness, optical spectroscopy absorption from UV to IR were used to characterize each step of the process sol-wet, gel-dry gel-glass. SiO2 glasses materials prepared in this way present optical quality similar to that obtain commercially
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-04-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.