Disertación de Maestría
DOI
10.11606/D.54.1979.tde-16042014-173234
Documento
Autor
Nombre completo
Maria Keiko Udo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1979
Director
Tribunal
Souza, Milton Ferreira de (Presidente)
Mokross, Bernhard Joachim
Morato, Spero Penha
Título en portugués
Sobre a cristalização de esferas de poliestireno em suspensão aquosa
Palabras clave en portugués
Cristalização
Esferas de poliestireno
Suspensão aquosa
Resumen en portugués
Foi estudada a cristalização de suspensões aquosas de esferas de poliestireno (850Å, 910Å e 1090Å de diâmetro) no limite de baixas concentrações -1011 a 1013 esferas / cm3. A dependência do parâmetro de rede com a concentração original (n) da suspensão aquosa apresenta uma transição de fase da fase bcc para fcc, conforme já foi observada por outros autores. Observamos também que durante a cristalização a concentração de esferas no cristal Ra sistematicamente maior do que na solução original, portanto a água estaria sendo expelida para a solução durante a cristalização. Baseado nestas observações nós propomos um modelo de cristalização onde os cristalites (concentração n1) estão em equilíbrio termodinâmico com uma solução com concentração n2 (n1> n > n2), dando para cada concentração inicial um diferente parâmetro de rede determinado por este equilíbrio. Nossos resultados mostraram que o coeficiente de expulsão da água durante a cristalização é dependente do raio da esfera. Para realizar as medidas de parâmetro de rede nós adaptamos para as nossas condições particulares o método de Debye-Scherrer usado em difração de raios-X por cristais. O equivalente à fonte de raios-X era um laser de Argônio com comprimentos de onda variáveis. Diversas experiências novas são sugeridas.
Título en inglés
About crystallization of polystyrene spheres in aqueous suspension
Palabras clave en inglés
Aqueous suspension
Crystallization
Polystyrene spheres
Resumen en inglés
The crystallization of aqueous suspensions of polystyrene spheres 850Å, 910Å and 1090Å of diameter) was studied in the limit of low concentration -1011 to 1013 spheres / cm3. The dependence of the lattice parameter with the original concentration (n) of the aqueous suspension shows a phase transition from bcc to fcc phase as it was already been observed by others authors. We also observed that during crystallization the concentration of spheres in the crystal was systematically higher than in the original solution, showing that water should be expelled toward the solution during crystallization where the crystallites (concentration n1) are in thermodynamic equilibrium with a solution with concentration n2 (n1> n > n2) giving for each initial concentration a different lattice parameter determined by this equilibrium. Our results showed that coefficient of water rejection during crystallization is dependent on the sphere radius. In order to make the measurements of the lattice parameter we adapted to our particular conditions the Debye-Scherrer method used in X-ray diffraction of crystals. The equivalent to the X-ray source was a tunable Argon laser. Several new experiments are suggested.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MariaKeikoUdoM.pdf (4.44 Mbytes)
Fecha de Publicación
2014-04-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.