Disertación de Maestría
DOI
10.11606/D.54.1987.tde-14102009-113933
Documento
Autor
Nombre completo
Alfredo Jorge
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1987
Director
Título en portugués
Medidas de correntes termo-estimuladas e isotermas no ar em filmes de polivinilideno de fluor (PVF2).
Palabras clave en portugués
Correntes termoestimuladas
Filmes
PVF2
Resumen en portugués
Um elenco bastante diverso de medidas experimentais isotermas e termicamente estimuladas, com o intuito de estudar efeitos em processos de polarização em filmes de PVF2 foi realizado. A análise dos resultados conduziu a levantar as seguintes hipóteses. Nas amostras Fase Alfa, os processos de polarização existentes em medidas de TSC no ar, estão ligados às orientações dipolares no interior do material; enquanto que para as amostras na Fase Beta, esses processos estão ligados a cargas espaciais que não "abandonam" o material. No segundo caso ajustou-se aos resultados experimentais, um modelo de cinética de primeira ordem, obtendo vários parâmetros elétricos importantes desse material.
Título en inglés
Measurements of termoestimulated currents and isotherms in air and in films of polyvinylidene fluoride (PVF2)
Palabras clave en inglés
Films
PVF2
Termoestimulated current
Resumen en inglés
A great number of TSC and isotermal decays were carried out in ambient air, aimed to investigate the polarization processes in thin PVF2 foils. The analysis of the results seems to indicate the following: For Alfa-samples, the polarization processes is connected with dipole orientation in the bulk of the material, while, for Betha-samples, these processes are partially due to motion of carriers inside the material. For this case a fitting assuming a first order kinectic process was successful, allowing to derive several parameters.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AlfredoJorgeM.pdf (2.95 Mbytes)
Fecha de Publicación
2009-12-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.