Disertación de Maestría
DOI
10.11606/D.54.1989.tde-06022014-101453
Documento
Autor
Nombre completo
Lígia de Oliveira Ruggiero
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1989
Director
Tribunal
Li, Maximo Siu (Presidente)
Aegerter, Michel Andre
Carmo, Luiz Carlos Scavarda do
Título en portugués
Estudo da presença de pares de Cu+ - OCN- e Cu+ - CN- no cristal de KCl
Palabras clave en portugués
CN- em KCl
OCN- e Cu+
Pares de Cu+
Resumen en portugués
O presente trabalho mostra um estudo sobre a presença de pares de íons de CN- - Cu+ e OCN- -Cu+, em cristais de KCl, usando técnicas de medidas de corrente de despolarização termoestimulada (I.T.C.) e Absorção óptica. A detecção destes pares foi feita através de um estudo sistemática de correlação entre as diferentes amostras aqui usadas: KCl + 1% KCN; KCl + 1% CuCl; KCl + 1% KOCN; KCl + 1% KOCN + 1% CuCl e KCl + 1% KCN + 1% CuCl. Deve ser ressaltado que a última amostra apresenta um tipo de impureza não intencional OCN- , cuja associação com o íon Cu+ também é observada. Na absorção ótica observamos bandas à temperatura ambiente em 210, 228, 242, 252, 260 e 290 nm para o cristal de KCl + 1% CuCl + 1% KCN, sendo que para o cristal de KCl + 1% KOCN + 1% CuCl não foi observado o último pico. As diferentes bandas são atribuídas às possíveis interações entre Cu+ e CN-, bem como Cu+ e OCN-. Quanto à técnica de ITC, as curvas obtidas por esta, para os três últimos cirstais citados acima, foram melhor ajustadas pela somatória de duas curvas singulares de ITC, cujas temperaturas de pico estão nas posições de 53 e 55 K; 54,3 e 56,6 K; 53,3 e 56,1 K, respectivamente. Em KCl + 1% KOCN a curva de mais baixa temperatura (curva 1) de ITC é atribuída à molécula (16O12C14N-) e a curva de mais alta temperatura (curva 2) é atribuída à molécula isotrópica (18O12C14N-). Para as amostras de KCl + 1% KOCN + 1% CuCl a curva 1 foi atribuída ao OCN- isolado e a curva 2 ao Cu+ perturbado pela presença do OCN-. Quanto ao cristal de KCl + 1% KCN + 1% CuCl, as duas técnicas propostas não foram suficientes para identificar a presença de pares Cu+ - CN-, necessitando, desta maneira, da utilização de outra técnica experimental, como por exemplo a da luminescência. A correlação dos resultados experimentais foi feita através dos parâmetros determinados do momento de dipolo (p), energia de ativação (Ea∗) e a temperatura de pico (Tm∗)
Título en inglés
Study of Cu+ - OCN- and Cu+ - CN- pairs in KCl crystal
Palabras clave en inglés
Cu+ - CN-
Cu+ - OCN-
Pairs in KCl single crystal
Resumen en inglés
The present work gives a study on CN- - Cu+ and OCN- -Cu+ coupled pairs doped KCl single crystal, by using Ionic Thermal Current (I.T.C.) and Optical absorption techniques. These pairs were detected through a systematic correlation study between different samples: KCl + 1% KCN; KCl + 1% CuCl; KCl + 1% KOCN; KCl + 1% KOCN + 1% CuCl and KCl + 1% KCN + 1% CuCl, were the last sample shows unporposely doping OCN-, compled with Cu+. The observed optical absorption bands, at room temperature, were in 210, 228, 242, 252, 260 and 290 nm for KCl + 1% CuCl + 1% KCN crystal. Only the last absorption band was not seen in KCl + 1% KOCN + 1% CuCl samples. Diferent bands are associated with possible interactions between Cu+ and CN-, as also Cu+ with OCN-. The ITC curves for the last three crystals were better fitted with two single ITC´s curves, whose temperature peaks are at 53 and 55 K; 54,3 and 56,6 K; 53,3 and 56,1 K, respectively. The lowest temperature ITC band (curve 1) in KCl + 1% KOCN is attributed to the (16O12C14N-) molecule and the highest temperature ITC band (curve 2) is due to the (18O12C14N-) isotropic molecule. For KCl + 1% KOCN + 1% CuCl samples curve 1 was associated with isolated OCN- and curve 2 with Cu+ perturbed with OCN-. With KCl + 1% KCN + 1% CuCl, the two techniques were not good enough to identify Cu+ - CN-, compling, it should be necessary to apply another type of techniques, like luminescence. The correlations of the experimental results were done through the determination electric dipole moment (p), activation energy (Ea∗) and temperature peak (Tm∗) parameters
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
LigiadeOliveiraM.pdf (3.91 Mbytes)
Fecha de Publicación
2014-02-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.