Doctoral Thesis
DOI
10.11606/T.46.2010.tde-01032011-144813
Document
Author
Full name
Ludmila de Carvalho Fidale
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2010
Supervisor
Committee
El Seoud, Omar A (President)
Areas, Elizabeth Pinheiro Gomes
Petri, Denise Freitas Siqueira
Ramos, Ludmila de Araújo
Zaniquelli, Maria Elisabete Darbello
Title in Portuguese
Biopolímeros modificados: aspectos de derivatização de celulose sob condições homogêneas de reação
Keywords in Portuguese
Ativação
Derivatização
Dissolução
Líquido iônico
Reação homogênea
Abstract in Portuguese
Esta tese tem como objetivo a derivatização da celulose sob condições homogêneas de reação, através de um método simples, reprodutível e eficiente. As três etapas de derivatização da celulose (ativação, dissolução, e reação) foram estudadas com ênfase na relação entre a estrutura do biopolímero, as condições da reação e as propriedades dos derivados obtidos. Foi realizado estudo do intumescimento de celuloses (microcristalina, algodão, eucalipto, algodão mercerizado e eucalipto mercerizado) em solventes próticos e apróticos. O intumescimento foi correlacionado com as propriedades dos solventes. Nos próticos, as celuloses nativas e mercerizadas foram sensíveis aos mesmos quatro descritores (acidez, basicidade, dipolaridade/polarizabilidade e volume molar), porém, a contribuição relativa dessas propriedades foi diferente, sendo que no caso da celulose MC e das nativas a dipolaridade/polarizabilidade foi mais significativo e para as celuloses mercerizadas o volume molar foi o descritor mais importante. Para o intumescimento em solventes apróticos, para as celuloses mercerizadas, boas correlações foram obtidas empregando apenas um descritor (dipolaridade/polarizabilidade). No intumescimento intracristalino, investigamos as mudanças nas propriedades físico-químicas após a mercerização. Este tratamento resultou em: ocorreu aumento no teor de α-celulose; diminuição da cristalinidade; redução da espessura da fibra; remoção de fragmentos da superfície; aumento na área superficial. Salientamos que não ocorre uma diminuição significativa no grau de polimerização das celuloses. Empregamos uma nova classe de solvente (líquidos iônicos) para a dissolução e subsequente funcionalização da celulose. Tanto na dissolução por aquecimento térmico ou por micro-ondas a integridade física da celulose foi mantida. Alem disto, observamos que a dissolução facilita a acessibilidade/reatividade da celulose, pois ocorre a diminuição do índice de cristalinidade e o aumento da área superficial. O uso de aquecimento por micro-ondas mostrou-se mais rápido e eficiente do que aquecimento térmico, sendo que tempo necessário para a dissolução e acilação da celulose foi de 25 a 30% menor daquele com aquecimento térmico. O líquido iônico (AlBuImCl) mostrouse um excelente solvente em termos de controle do GS e reprodutibilidade do mesmo. Realizou-se um estudo da dependência das propriedades dos acetatos de celulose e seus filmes com o grau de substituição do biopolímero. Foram empregadas sondas solvatocrômicas e medidas térmicas para investigar as propriedades de filmes de acetatos de celulose. Os resultados obtidos mostraram que a dependência de tais propriedades sobre o grau de substituição dos acetatos de celulose pode ser descrita por equações simples. Por fim, desenvolveu-se um método simples, rápido, e preciso para a determinação do GS de ésteres de celulose (acetato, butirato e hexanoato), através do uso de sondas solvatocrômicas
Title in English
Modified biopolymers: aspects of cellulose derivatization under homogeneous reaction conditions
Keywords in English
Activation
Derivatization
Dissolution
Homogeneous reaction
Ionic liquid
Abstract in English
The objective of this thesis is to study some aspects of the derivatization of cellulose under homogeneous reaction conditions. The three steps of this reaction scheme (activation, dissolution and derivatization) were studied, with emphasis on the relationship between the biopolymer structure, the conditions of the reaction and the properties of the products. Swelling of different celluloses (microcrystalline (MC), cotton linter, eucalyptus, cotton linter mercerized, eucalyptus mercerized) by protic and aprotic solvents was determined. The results were correlated with a series of solvent descriptors. For protics solvents, although native and mercerized celluloses are sensitive to the same set of four solvent properties (acidity, basicity, dipolarity/polarizability, and molar volume), the relative contributions are different; π* is most important for MC and native celluloses, VS is most important for mercerized celluloses. Because of absence of hydrogen-bon donation by aprotics solvents, a smaller number of solvent descriptors is required in order to describe cellulose swelling. For example, the swelling of mercerized cellulose can be reasonably described by a single descriptor (dipolarity/polarizability). The effect of mercerization on cellulose properties was investigated; it leads to: increase of α-cellulose content; decrease of Ic; decrease of fiber cross section, smoothing of its surface, and increase of its surface area. The ionic liquid 1-allyl-3-(1-butyl)imidazolium chloride showed to be a convenient reaction medium for the dissolution and derivatization of cellulose, with reproducible easily controlled degree of substitution, DS. The physical integrity of the cellulose is maintained during dissolution by using either "conventional" or convection-, or microwave heating. Compared with the former, MW irradiation has resulted in considerable decrease in dissolution- and reaction times. The value DS was found to be DSethanoate > DSpropanoate > DSbutanoate. The values of DSpentanoate and DShexanoate were found to be slightly higher than DSethanoate. The dependence of the properties of cellulose acetates and their films on the degree of biopolymer substitution was investigated. Solvatochromic probes and thermal analysis have been employed. The results showed that the dependence of the properties (solvatochromic parameters and thermal properties) of CAs on their DS can be described by simple equations; a consequence of the substitution of the OH by the ester group. Finally, an expedient, accurate method for the determination of the degree of substitution of cellulose carboxylic esters (ethanoate, butanoate and hexanoate) was developed, using Uv-vis spectroscopy (dye perichromism)
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-06-13
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.