Tesis Doctoral
DOI
10.11606/T.46.2018.tde-09082018-102116
Documento
Autor
Nombre completo
Christian Graziani Garcia
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2002
Director
Tribunal
Iha, Neyde Yukie Murakami (Presidente)
Batista, Alzir Azevedo
Constantino, Vera Regina Leopoldo
Andrade, Adnei Melges de
Faria, Dalva Lucia Araujo de
Título en portugués
Desenvolvimento de célula solar fotoeletroquímica com TiO2 sensibilizado por corantes
Palabras clave en portugués
Células solares (Desenvolvimento)
Corantes
Energia solar
Fotoquímica inorgânica
Resumen en portugués
O trabalho apresenta o desenvolvimento de células solares fotoeletroquímicas baseadas na sensibilização de n-TiO2 por corantes sintéticos e naturais. Abrange as etapas envolvidas na sua obtenção, desde a preparação dos compostos sensibilizadores, filmes semicondutores e meio eletrolítico, até a montagem e medidas de eficiência, com a otimização dos diversos componentes do sistema, num arranjo do tipo sanduíche. O fotoanodo consiste num filme de TiO2 nanocristalino sensibilizado pelo corante num substrato condutor. O contraeletrodo é composto de um substrato condutor recoberto com camada transparente de platina. Entre os eletrodos é disposta a camada de eletrólito, geralmente solução de l2/Lil em acetonitrila. A espessura do filme de semicondutor é controlada com os métodos empregados na deposição de sua dispersão. A transparência final depende ainda do método de preparação das dispersões. Utilizando as espécies cis-[(dcbH2)2RuLL')2+, dcbH2 = 4,4'-(CO2H)2-2,2'bipiridina e L/L' = cianopiridina, quinolina e H2O, como sensibilizador, obteve-se conversão eficiente de luz visível em eletricidade com valores de IPCE de até 50 % entre 400 e 550 nm. Os processos de transferência e recombinação de elétron na interface sensibilizador/semicondutor foram investigados por experimentos com técnicas resolvidas no tempo empregando sensibilizadores ancorados aos filmes transparentes de TiO2. O trabalho envolveu ainda incorporações técnicas para aumentar a eficiência da célula, como filamentos metálicos protegidos e a combinação de unidades independentes numa associação modular, que são objetos de patentes depositadas.
Título en inglés
Development of photoelectrochemical solar cell with dye-sensitized TiO2
Palabras clave en inglés
Dyes
Inorganic photochemistry
Solar cells (Development)
Solar energy
Resumen en inglés
This work presents the development on photoelectrochemical solar cells based on sensitization of n-TiO2 by synthetic and natural dyes. It comprises several steps involved in the fabrication and assembling of the cells in a sandwich-type design. Preparation of sensitizers, semiconductor films and electrolyte media, as well as efficiency measurements and optimization of several components are presented. The photoanode consists of a dye-sensitized nanocrystalline n-TiO2 film onto a conductive substrate. The counterelectrode is a conductive substrate covered with a thin, transparent platinum layer. The electrolyte layer, usually l2/Lil in acetonitrile, is placed between the electrodes. The deposition process of the semiconductor dispersion onto the substrates regulates the resulting thickness of the film. The final transparency is also controlled by the procedure employed in the preparation of the semiconductor dispersion. The species cis-[(dcbH2)2RuLL']2+, dcbH2 = 4,4'-(CO2H)2-2,2'-bipyridine and L/L' = 4-cyanopyridine, quinoline and H2O, were employed as sensitizers resulting in IPCE (Incident Monochromatic Photon to Current Conversion Efficiency) values as high as 50 % from 400 to 550 nm. Electron transfer and recombination processes across the semiconductor/sensitizer interface were investigated with time-resolved experiments employing transparent films of n-TiO2 sensitized by the anchored species. Other approaches aiming improvements in efficiencies and the preparation of photoelectrochemical solar cells for different applications or through environmentally friendly processes are discussed. The use of protected metallic filaments and the modular arrangement of single cells are issues of patents.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-08-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.