Tesis Doctoral
DOI
10.11606/T.46.2016.tde-28012016-170840
Documento
Autor
Nombre completo
Hector Alexandre Chaves Gil
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1998
Director
Tribunal
Kawano, Yoshio (Presidente)
Catalani, Luiz Henrique
Ferreira, Guilherme Fontes Leal
Galembeck, Fernando
Matos, Jivaldo do Rosario
Título en portugués
Estudo das modificações estruturais induzidas pela radiação de alta energia sobre o copolímero P(VDF-TrFE)
Palabras clave en portugués
Copolímero
Espectroscopia fotoacústica
Espectroscopia Raman
Espectroscopia vibracional
P(VDF-TrFE)
Polímeros (Química orgânica)
Raios-X
Resumen en portugués
Filmes de poli(fluoreto de vinilideno-co-trifluoretileno), P(VDF-IrFE), com uma razão molar 70/30 de VDF e IrFE, respectivamente, foram expostos à radiação-X sob vácuo em uma ampla faixa de doses de irradiação. Este é um copolímero estatístico e semi-cristalino que possui a especial característica de cristalizar espontaneamente numa estrutura ferroelétrica. Ele também possui uma transição de fase ferro-paraelétrica detectável, definida como a temperatura de Curie (Tc). Devido a estas características tem despertado considerável interesse, em especial na área da eletrônica como elemento transdutor. As modificações induzidas foram investigadas por espectroscopia fotoacústica no infravermelho (FT-IR/PAS), assim como FI-IR por transmitância, calorimetria exploratória diferencial (DSC), termogravimetria (IG), difração de raios-X, UV/Visível e espectroscopia Raman. As técnicas espectroscópicas vibracionais (fotoacústica no IR, Raman e absorção no IR) foram utilizadas na identificação de bandas relacionadas às regiões cristalinas e amorfas, formação e rompimento de ligações e presença de novos grupos funcionais. Nos espectros IR e Raman são observadas duas bandas que estão relacionadas às regiões cristalinas e sofrem mudanças nas suas intensidades relativas de acordo com a dose de radiação. Essas mudanças podem ser interpretadas como aumento ou diminuição do grau de cristalinidade, e também em termos de modificações de arranjos cristalinos. A difração de raio-X mostrou o aparecimento de um pico, próximo àquele da fase ferroelétrica, sob aumento da dose de radiação, devido a um processo de modificação do arranjo cristalino acima da dose de 480 kGy. Foi observado um aumento de intensidade no referido pico de difração, correspondendo a um aumento do grau de cristalinidade da amostra. As curvas de DSC mostraram picos endotérmicos correspondentes a fusão e transições de fases que, através de suas variações, possibilitam avaliar os efeitos da irradiação com raios-X. Os espectros UV/Visível mostraram absorções dos cromóforos cujas intensidades de banda aumentam com a dose de radiação e diminuem durante o envelhecimento da amostra. Os dados indicam que a radiação-X induz uma modificação no arranjo cristalino do P(VDF-TrFE). Tal modificação, é provavelmente uma mudança de estrutura ferroelétrica para outra, paraelétrica.
Título en inglés
Study of structural modifications induced by high energy radiation on the copolymer P (VDF-TrFE)
Palabras clave en inglés
Photoacoustic spectroscopy
Polymers (Organic chemistry)
PVDF-TrFE) copolymer
Raman spectroscopy
Vibrational spectroscopy
X-rays
Resumen en inglés
Poly(vinylidene fluoride-co-trifluoroethylene) films, P(VDF-TrFE), with a molar ratio 70/30 of VDF and TrFE units, respectively, were exposed to X-ray radiation under vacuum in a wide range of irradiation doses. This is a statistic semi-crystalline copolymer and displays the unique feature of a spontaneous crystallization into a ferroelectric structure. It also possesses a detectable ferro-paraelectric transition, the Curie temperature (Tc). Due to these characteristics considerable interest in such copolymer has been generated, specially in electronics as a transducer element. The induced modifications were investigated by Fourier transform infrared photoacoustic spectroscopy (FT-IR/PAS) as well as transmittance FT-IR, differential scanning calorimetry (DSC), thermogravimetry (TG), X-ray diffraction, UV/Visible and Raman spectroscopies. The spectroscopic vibrational techniques (FT-IR/PAS, FT-IR and Raman) were used to identify bands related to crystalline and amorphous regions, bond formation, bond scission and presence of new functional groups. In both IR and Raman spectra were observed a couple of bands related to the crystalline regions that undergo changes of relative intensities with the radiation dose. These changes may be interpreted as an increase or decrease of the crystallinity degree, and also modifications of crystal structure. X-ray diffraction showed a new peak, close to that of the ferroelectric phase, under increasing radiation doses, due to a modification of crystal structure process above 480 kGy dose. An increase in the intensity of the former diffraction peak was observed, corresponding to an increase in the crystallinity degree. The DSC curves showed the endothermic peaks corresponding to the melting and the phase transitions, whose variations allow an evaluation of the effects of X-ray radiation. UV/Visible spectra showed chromophores absorptions whose band intensities increase by radiation dose and decrease during sample's aging. The data indicate that P(VDF-TrFE) under X-ray radiation exposition undergoes a crystal structure modification, probably a change of a ferroelectric structure to another one, paraelectric.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-01-28
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2023. Todos los derechos reservados.