Disertación de Maestría
DOI
10.11606/D.46.2018.tde-27082018-094758
Documento
Autor
Nombre completo
Carlos Nalvo Machado Junior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2002
Director
Tribunal
Kawano, Yoshio (Presidente)
Demarquette, Nicole Raymonde
Petri, Denise Freitas Siqueira
Título en portugués
Estudo térmico e vibracional do ionômero nafion
Palabras clave en portugués
Análise espectroscópica
Célula combustível
Espectroscopia vibracional
Ionômero nafion
Método termoanalítico
Polímeros condutores
Resumen en portugués
O Nafion é um ionômero constituído por uma matriz de politetrafluoroetileno (PTFE) contendo ramificações laterais terminadas em grupos sulfônicos. Neste trabalho, a membrana na forma ácida e nas formas salinas (Li+, Na+, K+, Rb+ e Cs+) foram analisadas, via espectroscopia vibracional e análise térmica. Para proceder à análise vibracional, dividiu-se o ionômero em três grupos, cada qual pertencente a um grupo pontual distinto: o grupo sultanato (C3v) ; o grupo éter (C2v) e a matriz fluorocarbônica D(14π/15). O grupo sulfonato apresenta modos vibracionais de estiramento simétrico (1060 cm-1) e de estiramento degenerado (na região de 1300 cm-1). O Nafion apresenta dois grupos éter, os quais deram origem no espectro a duas bandas: uma em 984 e outra na região de 970 cm-1. Verificou-se que apenas a banda em 970 cm-1 sofre uma influência mais direta do ambiente iônico. A atribuição das bandas da matriz polimérica foi feita considerando-se que a cadeia de PTFE apresenta estrutura helicoidal (157) . Nesta estrutura são previstas a existência de quatro espécies de simetria que apresentam atividade nos espectro Raman e infravermelho. No Raman são ativos os modos de espécie A1, E1 e E2 e no infravermelho são ativos os modos de espécie A2 e E1. A análise térmica dividiu-se em: termogravimetria e calorimetria exploratória diferencial. A termogravimetria mostrou que a membrana na forma ácida apresenta um padrão de decomposição distinto das membranas nas formas salinas. A calorimetria exploratória diferencial mostrou que a membrana na forma ácida apresenta três eventos endotérmicos: em 134ºC, em 250ºC e o último em 325ºC. Na membrana nas formas salinas apenas o primeiro pico endotérmico é bastante evidente, o segundo pico é pouco pronunciado e o terceiro está completamente ausente.
Título en inglés
Thermal and vibration study of the nafion ionomer
Palabras clave en inglés
Conductive polymers
Fuel cell
Nafion Ionomer
Spectroscopic analysis
Thermoanalytical method
Vibrational spectroscopy
Resumen en inglés
Nafion is an ionomer that consists of a polytetrafluoroethylene (PTFE) backbone with side chains terminated with a sulfonate group. In this work, Nafion in acid and saline forms (Li+, Na+, K+, Rb+ e Cs+) forms were investigated by vibrational spectroscopy, thermogravimetry and differential scanning calorimetry. To proceed to the vibrational analysis the ionômero was splitted into three regions and which one has its own symmetry group. Sulfonate group (C3v), ether group (C2v) and the polymeric matrix D(14π/15). The sulfonate group presents two modes: the symmetric stretching (1060 cm-1) and the degenerated stretching (around 1300 cm-1). Nafion has two ether groups which originated two bands: one in 984 and the other in 970 cm-1. We verify that only the band in 970 cm-1 is affected by the ionic ambient. The assignment of the polymeric band was made considering that the PTFE has helicoidal structure (157). In this structure four symmetry species are predicted. In Raman spectra the following species are active: A1, E1 and E2 and the infrared are active the species: A2 and E1. Thermal analysis consisted of thermogravimetry and differential scanning calorimetry. Thermogravimetry shows that water content is dependent of cation change. Thermogravimetry also shows that the membrane in the acid and saline forms have different mechanisms of decomposition. Differential scanning calorimetry of Nafion-H shows three endothermic peaks: the first in 134ºC, the second in 250ºC and the last in 325ºC. Nafion saline forms shows only the first peak.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-08-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.