Mémoire de Maîtrise
DOI
10.11606/D.46.2006.tde-24012007-142747
Document
Auteur
Nom complet
Juliana Vieira Custódio
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2006
Directeur
Jury
Agostinho, Silvia Maria Leite (Président)
Freire, Renato Sanches
Wolynec, Stephan
Titre en portugais
Viabilidade do emprego do benzotriazol (BTAH) e do cloreto de dodecilamônio (DAC) como inibidores de corrosão para o aço-carbono em processos de hidrojateamento e na composição de tintas á base d´água
Mots-clés en portugais
Aço-carbono
Corrosão
Eletroquímica
Hidrojateamento
Tintas
Resumé en portugais
Foi estudada a viabilidade do emprego do benzotriazol (BTAH) e da mistura BTAH/cloreto de dodecilamônio (DAC) como inibidores de corrosão do aço-carbono 1005. Os inibidores foram testados em três situações: em processos de hidrojateamento e jateamento, quando adicionados a um primer acrílico de base água e a um filme prévio sobre a superfície do aço, antes da aplicação do primer. O aço foi estudado em meios de água com diversos graus de pureza na ausência e presença de BTAH e de BTAH/DAC. Foram feitos ensaios de perda de massa, medidas de potencial de circuito aberto, de tensão superficial e de condutividade, polarização potenciostática e potenciodinâmica, espectroscopia de impedância eletroquímica, microscopia eletrônica de varredura e espectroscopia por dispersão de energia. O melhor desempenho do BTAH como inibidor é em água bidestilada com eficiência da ordem de 100%; a adição de DAC às soluções contendo BTAH diminui a ação inibidora para 50%. A adição de BTAH ao primer impede o efeito de barreira deste e a eficiência inibidora se torna comparável à observada quando o aço, sem revestimento, é imerso no eletrólito contendo BTAH. O BTAH promove a formação de um filme prévio sobre o aço quando exposto a uma atmosfera úmida e depois imerso em água bidestilada contendo BTAH. A presença deste filme não modifica as características protetoras do primer comercial.¶
Titre en anglais
Viability of the employ of benzotriazole (BTAH) and BTAH/dodecylammonium chloride (DAC) as corrosion inhibitors for carbon steel on hydroblasting processes and water based paint composition
Mots-clés en anglais
Carbon steel
Corrosion
Electrochemistry
Hydroblasting
Resumé en anglais
The viability of the use of benzotriazole (BTAH) and BTAH/dodecylammonium chloride (DAC) as corrosion inhibitors for 1005 carbon steel was studied. The inhibitors were tested on blasting and hydroblasting processes, when added to waterborne acrylic primer and as a film on the metal surface before the application of the paint. The steel was studied in different purity grade water in the absence and in the presence of BTAH and BTAH/DAC. Weight loss experiments, open circuit potential, tensiometry, conductimetry, anodic and cathodic potentiostatic polarization curves, anodic potentiodynamic polarization curves, impedance spectroscopy, scanning electron microscopy and energy dispersive spectroscopy were used as techniques. The best performance of BTAH was observed in twice distilled water with about 100% inhibition efficiency; the addition of DAC to the solutions containing BTAH reduces the inhibitory effect to about 50%. When BTAH is added to the primer, the efficiency is similar to the one observed for the C steel without paint immersed in the same electrolyte containing BTAH. BTAH promotes the formation of a film when the steel is exposed to a humid atmosphere before immersion in twice distilled water containing BTAH. This film does not affect the features of the commercial primer.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
D.pdf (4.37 Mbytes)
Date de Publication
2007-02-07
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.