Master's Dissertation
DOI
10.11606/D.46.2005.tde-23052007-112206
Document
Author
Full name
Francisco Nascimento Lopes
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2005
Supervisor
Committee
Faria, Dalva Lúcia Araújo de (President)
Kawano, Yoshio
Souza, Luiz Antônio Cruz
Title in Portuguese
Espectroscopia Raman aplicada ao estudo de pigmentos em bens culturais: I - pinturas rupestres
Keywords in Portuguese
Degradação microbiológica
Espectroscopia Raman
Goetita
Hematita
Infravermelho
Oxalato de cálcio
Pigmentos minerais
Pinturas rupestres
Abstract in Portuguese
Neste estudo amostras coletadas de pinturas rupestres foram analisadas para identificação do material utilizado; análises da sua interação e de processos eventuais de degradação, além de atribuições quanto à sua origem, foram também feitas através da espectroscopia Raman. Pigmentos encontrados em pinturas rupestres em Minas Gerais foram identificados, junto a produtos de degradação microbiológica. A partir dos resultados, foi feita uma caracterização da transformação de desidratação do pigmento amarelo de goetita (α-FeOOH) a hematita (α-Fe2O3) por espectroscopia Raman na tentativa de contextualizá-la no problema da origem da hematita encontrada nas representações. Foram identificados os pigmentos calcita (CaCO3) para o branco, carvão vegetal para o preto, goetita (α-FeOOH) para o amarelo e hematita (α-Fe2O3) para o vermelho, que constituem basicamente a paleta de cores desse período. Produtos de degradação microbiológica foram identificados por espectroscopia Raman e no infravermelho por ATR como sendo whewellita (CaC2O4.H2O) e weddelita(CaC2O4.2H2O). A transformação topotática de goetita a hematita por aquecimento foi acompanhada por espectroscopia Raman in situ e ex-situ e infravermelho, na tentativa de caracterizar o processo quanto às fases formadas, possíveis marcadores, de maneira a complementar resultados da literatura que utilizaram outras técnicas, como difração de raio-X (XRD) e microscopia eletrônica de transmissão (TEM). Esse estudo foi realizado na tentativa de determinar a existência de possível manipulação térmica desses materiais como sugerido em trabalhos anteriores. Em particular, nos espectros Raman, o comportamento diferenciado da banda em torno de 660 cm-1 e a maior largura das bandas de uma maneira geral, presentes na chamada hematita desordenada, perfil que as amostras naturais coletadas apresentam, são marcadores do efeito de temperatura, uma vez que parecem estar ligados mais estreitamente ao deslocamento catiônico dos íons Fe do que ao rearranjo da gaiola octaédrica de oxigênios ao redor destes, durante a transição a partir de goetita. Esse comportamento dos espectros Raman é confirmado pelos padrões dos difratogramas de raio-X. Concluiu-se que esse desordenamento, entretanto, não é causado somente pela temperatura e, dessa forma, não pode ser usado para atestar inequivocamente como sendo resultado de processamento dos materiais (goetita).
Title in English
Raman spectroscopy applied to the study of pigments in cultural goods: I - rupestrian paintings
Keywords in English
Calcium oxalate
Goethite
Hematite
Infrared
Microbiological degradation
Mineral pigments
Raman spectroscopy
Rupestrian painting
Abstract in English
This dissertation reports the investigation carried out on samples collected from rupestrian paintings, aiming at the identification of materials used, their interaction and degradation. The technique of choice was Raman microscopy as it is a non-destructive tool, which provides the spatial resolution necessary for the study of heterogeneous samples. Pigments were identified together with products of microbiological degradation. Thermal convertion of goethite (yellow) to hematite (red) was followed by Raman spectroscopy in a tentative to address the issue of the provenance of red pigments (natural hematite or heated goethite) found in the paintings. White pigments were identified as calcite (CaCO3), whereas charcoal was used as black, goethite (α-FeOOH) as yellow and hematite (α-Fe2O3) as red. These pigments are usually found in rock art palletes. Degradation products from microbiological activity were identified by Raman microscopy and ATR infrared spectroscopy as being whewellite (CaC2O4.H2O) and weddelite (CaC2O4.2H2O). The topotatic transition from goethite to hematite was followed by in situ and ex-situ Raman and infrared spectroscopy, regarding the characterization of the phases formed, possible markers, aiming to complement the previous results reported in the literature using other techniques such as X-ray diffractometry (XRD) and transmission eletron microscopy (TEM). The main goal of the study of temperature effect on the Raman spectrum of goethite was to determine whether hematite was used as found in nature or was obtained by goethite heating as suggested in previous investigations. Particularly, the behavior of the 660 cm-1 band and a larger linewidth for bands in the spectrum, present in the disordered hematite and in the red pigments analysed, are markers of the thermal processing. These features seem to be related to the movement of iron ions and to the rearrangment of the octahedrical cage formed by oxygen atoms around them. Such conclusions are in agreement with X-ray data. Unfortunately, temperature is not the only factor to cause such structural disorder and, hence, it cannot be used as an unequivocal marker of thermal processing.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Dissert.pdf (3.24 Mbytes)
Publishing Date
2007-05-31
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.