Disertación de Maestría
DOI
https://doi.org/10.11606/D.46.2019.tde-23012019-092804
Documento
Autor
Nombre completo
Pablo Alejandro Fiorito
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2001
Director
Tribunal
Torresi, Susana Ines Cordoba de (Presidente)
Biaggio, Sonia Regina
Serrano, Silvia Helena Pires
Título en portugués
Construção de biossensores utilizando polímeros condutores eletrônicos
Palabras clave en portugués
Biossensores
Eletroquímica
Polímeros condutores
Resumen en portugués
Neste trabalho são elaborados biossensores para a detecção amperométrica de glicose. Para isso, imobilizou-se a enzima glicose oxidase em matrizes de polímeros condutores. Foram construídos sensores utilizando-se poli(pirrol) e poli(N-metilpirrol). Com o objetivo de substituir o oxigênio molecular na etapa de transdução do sinal, o ferroceno foi incorporado dentro do polímero condutor. Para isso, os polímeros foram elaborados utilizando misturas água-etanol como meio de polimerização. A inclusão do ferroceno no sensor resulta em maior sensibilidad à glicose (4,33 µA Mm-1 cm-2 para o biossensor preparado a partir da mistura água-etanol contendo o ferroceno e de 0,23 µA mM-1 cm-2 para o sensor sem ferroceno ). Por outro lado, permite o funcionamento do sensor a potenciais menores que no caso do sensor sem ferroceno (0,4 V para o sensor com ferroceno vs. 0,65 V para o caso sem ferroceno). O deslocamento do potencial de detecção para valores menos positivos não foi suficiente para evitar as interferências causadas pelos íons ascorbato e ureato. Para isto, mostrou-se 100% efetivo o recobrimento dos sensores com uma película de Nafion®. A sobreoxidação do poli(pirrol) também mostrou potencialidade para a eliminação de interferentes, embora o processo resulte na perda de sensibilidade, provavelmente causada pela desnaturação da enzima. Quando usado o poli(N-metilpirrol) como suporte para a enzima, obtiveram se melhores respostas, causadas pela possibilidade de se preparar filmes mais espessos, consequentemente de imobilizar maior quantidade de enzima, sem observar perda de resposta causada por problemas difusionais.
Título en inglés
Construction of biosensors using electronic conductive polymers
Palabras clave en inglés
Biosensors
Conductive polymers
Electrochemistry
Resumen en inglés
The present work describes the elaboration of a biosensor for glucose detection. The enzyme, glucose oxidase, was immobilized in different conducting polymers. Two different polymers were used: polypyrrole and poly(N-methilpyrrole ). With the aim of replacing the molecular oxygen in the transduction step, ferrocene has been immobilized within the conducting polymer. Once the ferrocenium was insoluble in water, in order to develop a different route, the electropolymerization was carried out in a mixture of water and ethanol (1:1). This procedure leads to a polymer with a poor electroactivity, detected by Raman experiments. The ferrocene addition in the sensor increases the sensitivity to the glucose determination (4,33 µA mM-1 cm-2 for the biosensor with ferroecene and 0,23 µA mM-1 cm-2 for the sensor without ferrocene). Alternatively, the sensor containing ferrocene allows to operate at less positive potentials than that one without ferrocene (+ 0,40 V and + 0,65 V, respectively). This potential shift was not enough to inhibit the interference caused by ascorbate and ureate ions. One method to avoid the interference problem was to recover the sensor with a very thin layer of Nafion. Also poly(pyrrole) overoxidation is a very efficient method to eliminate this interference, but this process leads to a sensitivity decrease dueto enzyme denaturation. A better response was observed for sensor assembled using the poly(Nmethyl-pyrrole) as the support for enzyme immobilization. This behavior was provoked by the thicker of polymer film formed leading to higher amount of immobilized enzyme. Even though, no diminution in the response was caused by diffusion problems.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-01-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.