Disertación de Maestría
DOI
10.11606/D.46.2007.tde-21052007-195731
Documento
Autor
Nombre completo
Daniela Manz
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Kawano, Yoshio (Presidente)
Catalani, Luiz Henrique
Wiebeck, Hélio
Título en portugués
Caracterização vibracional e térmica de filmes poliméricos utilizados como substrato em curativos adesivos
Palabras clave en portugués
Caracterização de materiais
Curativos adesivos
Filme polimérico
Módulo de elasticidade
Permeabilidade ao vapor d'água
Polímeros
Resumen en portugués
Um filme polimérico utilizado na fabricação de curativos adesivos não perfurados deve ter baixo módulo de elasticidade e boa permeabilidade ao vapor d' água. O baixo módulo de elasticidade garante sensação de maior conforto do produto em contato com a pele quando a pessoa que o está utilizando movimenta a parte do corpo sobre a qual está aplicado o curativo, principalmente a região das articulações, como joelhos e cotovelos. A importância de uma boa permeabilidade ao vapor d' água está relacionada, principalmente em curativos não perfurados, ao fato de que a pele perde água constantemente e, se o filme polimérico não permitir a saída dessa água ao meio ambiente, ocorrerá um fenômeno denominado maceração, que é a sensibilização excessiva da pele, causada pela hiper hidratação da mesma. O presente trabalho apresenta um estudo da permeabilidade ao vapor d' água, bem como a caracterização vibracional e térmica de um filme polimérico constituído por três polímeros diferentes, desenvolvido para substituir a poliuretana utilizada atualmente na produção de curativos adesivos não perfurados, com custo inferior. Os polímeros que constituem o filme foram caracterizados separadamente e alguns resultados obtidos, como Tm e a estrutura química dos polímeros Lotader® e Lotryl® foram comparados aos dados fornecidos pelo fabricante. Verificou-se que as propriedades de módulo de elasticidade e permeabilidade ao vapor d' água do filme desenvolvido são inferiores às da poliuretana inviabilizando a substituição. Entretanto, o trabalho proporcionou um melhor entendimento dos fatores que influenciam o módulo de elasticidade e a permeabilidade do novo material ao vapor d' água.
Título en inglés
Vibrational and thermal characterization of polymeric films used as substrate in adhesive tapes
Palabras clave en inglés
Adhesive tapes
Elasticity modulus
Materials characterization
Polymer
Polymeric film
Vapor water permeability
Resumen en inglés
A polymeric film must have low elasticity modulus and good water vapor permeation to be used in the production of non perforated adhesive tapes. Low modulus is desirable to provide comfort sensation as the consumer moves the part of his or her body in which the tape is applied on, mainly in the articulations regions, as elbows and knees. The importance of good water vapor permeation is related, mainly in the case of non perforated adhesive tapes with the continuous loss of water by the skin. If the film does not allow the release of the water continuously lost by the skin to the environment, the skin will become very sensitiveness as a result of over hydration. This work presents a study of water permeability and a thermal and vibrational characterization of a polymeric film composed of three different polymers developed to replace the adhesive not perforated polyurethane tape providing lower cost. Besides characterization a test of Water Vapor Transmission Rate (WVTR) was performed. Each polymer present in the film composition was analyzed and the results as Tm and chemical structure of Lotader® e Lotryl® were compared with the producer data. It was verified that the properties of elasticity modulus and water vapor permeability of the new material developed are worse than polyurethane so the substitution can not be performed. However, the work provided a better understanding of the factors that influences the elasticity modulus and water vapor permeability of the new material.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
dissertacaomanz.pdf (3.54 Mbytes)
pretexto.pdf (165.68 Kbytes)
significa que el fichero sólamente puede ser acceder dentro da la Universidad de São Paulo.
Fecha de Publicación
2007-07-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.