• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.46.2005.tde-06032007-220909
Documento
Autor
Nombre completo
Rita de Cássia dos Santos
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2005
Director
Tribunal
Kawano, Yoshio (Presidente)
Machado, Luci Diva Brocardo
Oliveira, Wanda de
Título en portugués
Caracterização vibracional e térmica de blendas de LDPE e m-LLDPE
Palabras clave en portugués
Análise térmica
Blendas de polietileno
Espectroscopia
Polímeros
Resumen en portugués
As blendas de polietileno de baixa densidade (LDPE) com o polietileno linear de baixa densidade (LLDPE) são utilizadas comercialmente com o objetivo de melhorar as propriedades finais dos produtos e o seu processamento, minimizar custos de produção tendo, como seu principal segmento, filmes para embalagens. O LLDPE utilizado neste trabalho foi sintetizado a partir do catalisador de metaloceno (m-LLDPE) que foi projetado para oferecer melhores propriedades mecânicas em relação ao LLDPE sintetizado por catalisador Ziegler-Natta. O m-LLDPE quando comparado ao LLDPE (Ziegler-Natta) apresenta resistência ao impacto do dardo quatro vezes maior e resistência ao rasgo de duas a quatro vezes maior, menor temperatura de selagem e melhor processabilidade. O LDPE tem boa processabilidade, oferece grande estabilidade ao balão durante o processo de extrusão por sopro e apresenta boas propriedades ópticas. Este trabalho reúne a caracterização térmica, vibracional e ensaios físico-químicos e mecânicos, do LDPE, m-LLDPE e as blendas de LDPE/m-LLDPE na proporção em massa de 75/25, 50/50 e 25/75. Na caracterização térmica foram utilizadas as técnicas: termogravimetria (TG), calorimetria exploratória diferencial (DSC) e análise térmica dinâmico-mecânica (DTMA). Na caracterização vibracional utilizou-se a espectroscopia fotoacústica no infravermelho (PAS-IR) e espectroscopia Raman. Foi utilizada a técnica de difração de raios-X (WAXD) para complementação dos resultados. Nos ensaios físico-químicos e mecânicos foram avaliadas as propriedades ópticas, rasgo de Elmendorf, propriedades de tração, resistência ao impacto do dardo e resistência da termossoldagem à tração. Por estas técnicas foram avaliadas as características térmicas e estruturais dos polímeros e seu comportamento nas blendas. Pela técnica de DSC foi possível verificar a imiscibilidade destas blendas. As técnicas PAS-IR, Raman e WAXD apresentam perfis espectrais semelhantes não possibilitando distinção entre as blendas de composição diferentes. Os resultados de DSC, PAS-IR e WAXD mostraram que não ocorrem mudanças significativas no grau de cristalinidade das blendas. Os ensaios de brilho 45° e opacidade mostram as boas propriedades ópticas do LDPE e suas blendas. Os ensaios mecânicos mostram que o m-LLDPE e suas blendas apresenta boas propriedades mecânicas e boa soldabilidade. Foi possível determinar a blenda que é melhor indicada para os vários segmentos do mercado de embalagens. As blendas de LDPE/m-LLDPE mais utilizadas pela indústria são as de 25/75 ou 75/25, para diferentes tipos de aplicação.
Título en inglés
Thermal and vibrational characterization of blends: Blends of low density polyethylene (LDPE) and linear low density polyethylene synthesized with the metallocene catalyst (m-LLDPE)
Palabras clave en inglés
Blends of polyethylene
Polymers
Spectroscopy
Thermal analysis
Resumen en inglés
Blends of low density polyethylene (LDPE) and linear low density polyethylene (LLDPE) are used commercially to improve the final properties of the products and their process, reduce the production cost having as their main segment packing film. The LLDPE used in this work was synthesized with the metallocene catalyst (m-LLDPE), which was projected to offer better mechanical properties in relation to the LLDPE synthesized by Ziegler-Natta catalyst. The m-LLDPE, when compared to the LLDPE (Ziegler-Natta) present dart impact strength four times stronger and the tearing resistance two to four times bigger, lower sealing temperature and good processability. The LDPE has good processability, offers great estability to the baloon during the process of blown extrusion and shows good optical properties. This work brings together the thermal and vibrational characterization, physical chemistry and mechanical tests, of the LDPE, m-LLDPE and the blends of LDPE/m-LLDPE in a 75/25, 50/50 and 25/75 parts by weight. In the thermal characterization several techniques were used: termogravimetry (TG), differential scanning calorimetry (DSC) and dynamic mechanical analyser (DTMA). In the vibrational characterization, the photoacoustic spectroscopy (PAS-IR) and Raman spectroscopy were used. The X-ray diffraction (WAXD) was used to complete the results. The physical chemistry and mechanical tests evaluated optical properties, Elmendorf tearing, tensile strength, dart impact strength, heat sealing strength and hot tack strength. With these techniques the thermal characterization and the polymer structure were evaluated as well as the blend behaviour. Using the DSC technique it was possible to observe that the blends are immiscible. The PAS-IR, Raman and WAXD techniques present spectral profiles not allowing a distinction between the blends with different composition. The results of DSC, PAS-IR and WAXD show that significant changes of crystallization of the blends haven' t occurred. The gloss 45° and haze show the good optical properties of the LDPE and their blends. The mechanical tests demonstrate the good mechanical properties and soldability of the m-LLDPE and their blends. It was possible to determine the blend that best fit the different segments of the packing market. The most frequently LDPE/m-LLDPE blends used by industry are the 25/75 or 75/25, for different applications.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
CAPA.pdf (11.77 Kbytes)
DISSERTACAO.pdf (2.51 Mbytes)
PRETEXTO.pdf (60.92 Kbytes)
Fecha de Publicación
2007-03-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.