Mémoire de Maîtrise
DOI
10.11606/D.43.2014.tde-20112014-105404
Document
Auteur
Nom complet
Gerson de Carli Proença de Almeida Pessotto
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2014
Directeur
Jury
Cornejo, Daniel Reinaldo (Président)
Béron, Fanny
Morelhao, Sergio Luiz
Titre en portugais
Propriedades magnéticas de filmes nanoestruturados de FeRh e FeRh/Fe
Mots-clés en portugais
Filmes finos
Física do estado sólido
Magnetismo
Materiais magnéticos
Resumé en portugais
As ligas de FeRh apresentam um comportamento não usual quando encontradas próximas da composição equiatômica, sendo observada uma transição de fase magnetoestrutural de primeira ordem, na qual o sistema passa de um estado antiferromagnético para um estado ferromagnético com a temperatura crítica próxima da temperatura ambiente. A temperatura crítica de transição é fortemente dependente da composição da liga, das técnicas de produção e dimensionalidade da amostra, além de fatores externos como pressão e campo magnético. No presente trabalho foram depositados, via magnetron sputtering, filmes de FeRh (monocamadas) e FeRh/Fe (bicamadas) sobre substratos monocristalinos de MgO (001), sendo utilizado duas temperaturas de deposição diferentes: 798 K e 913 K. A estrutura cristalina dos filmes foi analisada através de técnicas de medidas de difração de raios X (varredura &theta - 2 &theta, varredura em &phi e rocking curves) e as composições e espessuras dos filmes foram analisadas por medidas de RBS. A principal diferença morfológica encontrada entre as amostras foi uma melhor uniformidade na distribuição de orientações dos grãos cristalinos nos filmes depositados na temperatura mais elevada. As propriedades magnéticas, medidas por meio de um VSM equipado com um criostato e um forno, evidenciaram diferenças entre as amostras depositadas nas diferentes temperaturas mencionadas, observando-se variações significativas nas temperaturas de transição de fase e diferentes larguras dos ciclos térmicos. Também foi observado, em todas as amostras, coexistência de fases antiferromagnética e ferromagnética na camada de FeRh, principalmente na região de baixas temperaturas. As amostras depositadas em 798 K foram mais favoráveis à formação da fase FeRh antiferromagnética e, no caso das bicamadas, também apresentaram um melhor acoplamento entre as camadas de FeRh e Fe que as amostras depositadas em 913 K, favorecendo um incremento do campo coercivo e da magnetização remanente relativa do sistema.
Titre en anglais
Magnetic properties of FeRh and FeRh/Fe nanostructured films
Mots-clés en anglais
Magnetic materials
Magnetism
Solid state physics
Thin films
Resumé en anglais
FeRh alloys, near the equiatomic composition, present an unusual magneto structural first-order phase transition in which the system changes from antiferromagnetic to ferromagnetic state at a critical temperature close to ambient temperature. The critical transition temperature is strongly dependent on the alloy composition, production techniques and dimensionality of the sample, as well as external factors such as pressure and magnetic field. In the present work, FeRh (monolayers) and FeRh/Fe (bilayers) films were deposited on monocrystalline MgO (001) substrates, via magnetron sputtering, at two different deposition temperatures: 798 K and 913 K. The crystalline structures of the films were analyzed by using different techniques of X-ray diffraction (&theta - 2 &theta scan, &phi scan and rocking curves). The compositions and thicknesses of the films were analyzed by RBS measurements. The main morphological difference between the samples was a better uniformity in the distribution of crystalline grain orientations in the films deposited at higher temperature. The magnetic properties, which were measured by a VSM equipped with a cryostat and an oven, revealed differences between the samples obtained at different temperatures. Significant variations in the critical phase transition temperatures and different widths of thermal cycles were observed. It was also observed, in all samples, coexistence of antiferromagnetic and ferromagnetic phases in the FeRh layer, mainly at low temperatures. The samples deposited at 798 K were more favorable to the formation of the antiferromagnetic FeRh phase. In addition, for the bilayers deposited at 798 K, it was observed a better coupling between the FeRh and Fe layers in comparison to samples deposited at 913 K, favoring an increase in the coercive field and the remanence magnetization.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-11-24
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.