• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.43.2011.tde-15052012-154158
Documento
Autor
Nombre completo
Fabio Lombardi Maximino
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Santos, Antonio Domingues dos (Presidente)
Araki, Koiti
Araújo, Cid Bartolomeu de
Título en portugués
Caracterização de plasmons de superfície em filmes de metais nobres através de tunelamento ótico
Palabras clave en portugués
Filmes finos
Fotônica
Instrumento óptico
Plamônica
Resumen en portugués
Os metais nobres são admirados desde as culturas mais antigas por sua capacidade de refletir a luz. Com os desenvolvimentos na área da nanotecnologia se pode entender um pouco mais sobre a interação entre a luz e estes metais. Devido a esta interação foi criada a Plasmônica e a partir dela começaram os estudos acerca dos plasmons de superfície (SP). Estes estudos vêm gerando inúmeros desenvolvimentos nas pesquisas de gravação magneto-ótica, microscopia, detectores moleculares biológicos entre outras. Como os SPs são ondas evanescentes, eles precisam ser observados em campo próximo. Com o intuito de observar e compreender a propagação destes SPs foi utilizado um microscópio ótico de varredura em campo próximo (SNOM). Para isto, o SNOM foi adaptado para operar em modo de transmissão. A sonda do SNOM serviu de coletora de luz para que a partir de imagens óticas em amostras de Ag e Au pudéssemos caracterizar a propagação destes SPs na superfície do material e também a sua dependência com a distância de detecção. Os resultados mostraram que a propagação do SP é maior que 70m e a intensidade do SP na superfície do metal depende fortemente da rugosidade da amostra e de possíveis defeitos. Foi possível ainda estimar a que distância a partir da superfície da amostra, em que o SP decai para 1/e. Este resultado está de acordo com o esperado teoricamente, que prevê para a distância de propagação do SP, o valor de 420nm. Através do SP ainda foi possível analisar defeitos existentes na amostra. E pelas imagens topográficas do SNOM também foi possível observar os grãos de Ag e Au da amostra. Em posse destes resultados pudemos concluir que o SNOM é uma ótima ferramenta para a análise dos plasmons de superfície.
Título en inglés
Characterization of surface plasmons in noble metal films using optcal tunplening
Palabras clave en inglés
optical instrument
Photonic
Plasmonic
Thin films
Resumen en inglés
The noble metals are largely admired since ancient cultures because of its capability to reflect light. With the development of nanotechnology it is possible now to understand the interaction between these metals and light. Due to this strong interaction, the Plasmonic area was created and the studies on Surface Plasmons(SP) started. These studies are responsible for important new developments in magneto-optical recording, new optical microscopy apparatus, molecular biological sensors, among others. As SPs are evanescent waves, they need to be observed in near-field optics. For the observation and study of the propagation of these SPs a scanning near-field optical microscope (SNOM) was used. The SNOMs probe was used in collection mode so that we could characterize the propagation of SPs in the material surface and the dependence with the distance of detection in air, for thin films of Ag and Au. The results showed that the propagation of the SP inside the metallic film is beyon 70m. And the SPs intensity in the metal surface is strongly dependent on the roughness of the sample. It was also possible to estimate the distance from the samples surface the SP decay to 1/e. Our measurements agree to the theoretical calculation of 420nm for this distance. The SP made it possible to analyze existing defects on the sample. Furthermore, with the SNOM topographical images it was also possible to observe the grains of the policrystalline Ag and Au samples. From these results we could conclude that the SNOM is a very useful tool for the analysis of surface plasmons in thin films.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TeseMaximino.pdf (3.63 Mbytes)
Fecha de Publicación
2013-03-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2023. Todos los derechos reservados.