Thèse de Doctorat
DOI
10.11606/T.43.1997.tde-27022014-154140
Document
Auteur
Nom complet
Maria Cláudia Cerchiari Custódio
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 1997
Directeur
Jury
Hernandes, Antonio Carlos (Président)
Baldochi, Sonia Licia
Balzuweit, Karla
Leite, Jose Roberto
Missell, Frank Patrick
Titre en portugais
Síntese e Crescimento de Materiais Termoelétricos: Bi2Te3 e Soluções Sólidas de (Bi(1-x)Sbx)2 Te3
Mots-clés en portugais
Matéria condensada
Termoeletricidade
Resumé en portugais
Neste trabalho desenvolvemos um estudo detalhado do processo de síntese e preparação de cristais de Bi IND 2 Te IND 3 e (Bi IND (l-x)Sb IND x) Te IND 3, bem como uma abordagem qualitativa sobre a variação do coeficiente Seebeck em função do comprimento destes cristais. Preparamos cristais com condutividade tipo-p e tipo-n pela técnica de Bridgman em um sistema com gradiente de temperatura axial fixo (29 °C/cm), e em outro em que este parâmetro poderia ser alterado facilmente. Os cristais de telureto de bismuto tipo-p preparados no primeiro equipamento foram axialmente homogêneos em composição e coeficiente Seebeck, cuja intensidade média medida foi de 220 V/K. Os tipo-n apresentaram uma fase rica em telúrio em todo o seu comprimento e uma diminuição gradativa do coeficiente Seebeck. O aparecimento desta fase pode ser associado à instabilidade da interface sólido-líquido ou a um processo de superresfriamento constitucional localizado. Por outro lado, em nenhum dos cristais de Bi IND 2 Te IND 3 e (Bi IND (l-x)Sb IND x) Te IND 3, com condutividade tipo-p e n preparados no segundo sistema, houve presença da fase rica em telúrio e o máximo valor do coeficiente Seebeck foi superior ao relatado na literatura.
Titre en anglais
Synthesis Growth Thermoelectric Materials Bi2Te3 Solid Solutions (Bi (1-x) Sbx)2 Te3
Mots-clés en anglais
Condensed matter
Thermoelectricity
Resumé en anglais
ln this work, a detailed study on the synthesis and crystal growth process of Bi2Te3 e (Bi(l-x)Sbx)2 Te3 was carried out. The dependence of the Seebeck coefficient variation on the length crystal has been discussed in a qualitative way. P-type and n-type crystals were grown by the Bridgman technique using two different systems. In one system the axial temperature gradient was fixed, while in the other it could be adequately changed. The p-type bismuth tellurides grown in the first equipment were axially homogeneous in composition and Seebeck coefficient. Its average measured value was about 220 V/K. The n-type bismuth telluride presented a tellurium-rich phase in all of its extension and a decreasing Seebeck coefficient. The tellurium-rich phase can be related to solid-liquid interface instability or a constitucional supercooling. On the other hand, no Te-rich phase was detected in Bi2Te3 e (Bi(l-x)Sbx)2Te3 crystals grown in the second equipment. The maximum measured Seebeck coefficient of these materials was higher than the literature reported ones.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
45494Custodio.pdf (50.49 Mbytes)
Date de Publication
2014-02-28
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.