Tesis Doctoral
DOI
10.11606/T.43.1993.tde-22062012-150022
Documento
Autor
Nombre completo
Mario Ernesto Giroldo Valerio
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1993
Director
Tribunal
Blak, Ana Regina (Presidente)
Alves, Oswaldo Luiz
Monteiro, Waldemar Alfredo
Vieira Junior, Nilson Dias
Watanabe, Shigueo
Título en portugués
Agregacao de defeitos induzida pelo Al3+ Em solucões sólidas de fluoreto De cálcio com Yb3+ E La3+
Palabras clave en portugués
CaF2
Simuladores computacionais
TSDC
TSPC
Resumen en portugués
Apresentamos, pela primeira vez, estudos empregando Simulações Computacionais Estáticas e TSPC e TSDC de soluções sólidas de CaF2 com AIF (de 0,004 a 0,05 mol%), YbF3 e LaF? (- 0,l moi%). Os espectros de TSDC revelaram que: i) abaixo de 270K, as amostras só com Yb3+, La3+ e as multidopadas possuem a banda dos dipolos 1(0(0/11e dos defeitos 1j0/1/21, e as amostras pura ou só com A13+ não apresentam nenhuma banda; ii)acima de 270K, as amostras pura ou só com La3+ apresentam uma banda em 300K, atribuída a deslocações, e uma relaxação próxima a temperatura de polarização. As demais amostras apresentam uma banda predominante na faixa de 370 a 400K além desta última. TSPC combinado com TSDC mostrou que as bandas em 300K e entre 370 e 400K são devidas a fenômenos localizados de polarização e despolarização. Simulações computacionais mostraram que o A13+ não estabiliza dipolos isolados pois a energia de ligação dos agregados cubo-octaedrais é duas vezes menor do que a energia obtida para as terras raras. Nas soluções multidopadas, o AI3+ reduziu em mais de duas vezes a energia de ligação dos agregados cubo-octaedrais. As principais conclusões são: i)a banda entre 370 e 400K é devida ao agregado cubooctaedral; ii)o AI3+ gera preferencialmente agregados grandes do tipo cubo-octaedral; e iii)nas soluções multidopadas, o A13+ atua como "indutor" destes agregados.
Título en inglés
Aggregation defects induced by Al 3 + in solid solutions of calcium fluoride with Yb3 + and La3 +
Palabras clave en inglés
CaF2
computer simulators
TSDC
TSPC
Resumen en inglés
In the present work, we report, for the first time, measurements of TSDC and TSPC combined with Static Computer Simulation in the CaF2 solid solutions with one or more of the fluorides of aluminium (concentration range between 0.004 and 0.05 mol%), yterbium and lanthanum (concentration of about 0.1 mol%). The following behavior was found in the TSDC spectra: i) below room temperature, the Yb3+ and La3+ and the multidoped samples revealed the 1101011 1 dipole band and the 110/1/21 band while the A13+ and the pure samples displayed no bands; ii) from room temperature, the La3+ and the pure samples showed a depolarization band at 300K due to dislocations, while all the other samples exhibited a band near 370-400K. Combining TSPC and TSDC it was possible to verify that both relaxation bands are due to some kind of localized polarization fenomena. The Computer Simulation results made clear that it is improbable to find isolated A13+ dipoles since the binding energy of the cubo-octahedral cluster is more than two times lower than the values obtained for the rare earth ions. Concerning to the multidoped systems, the binding energies of the mixed cubo-octaedral clusters with A13+ and one of the rare earth ions, were less than half of the values obtained for the same cluster with the rare earth ions. The main conclusions of this work can be sumarized as follows: i) the 370-400K band is due to the cubo-octaedral cluster; ii) the A13+ gives rise mainly to cubo-octahedral clusters; and iii) inside the multidoped samples, the A13+ promotes the formation of cubo-octaedral clusters with the rare earth ions.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-06-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.