• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.43.1990.tde-20052014-135041
Documento
Autor
Nombre completo
Luiz Carlos Camargo Miranda Nagamine
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1990
Director
Tribunal
Rechenberg, Hercilio Rodolfo (Presidente)
Persiano, Aba Israel Cohen
Pontuschka, Walter Maigon
Título en portugués
Análise das populações dos sítios das ligas Sm IND.2 (Co,Fe) IND.17 por espectroscopia Mössbauer.
Palabras clave en portugués
Espectroscopia Mössbauer
Imãs permanentes
Ligas magnéticas de Sm2 Co17
Resumen en portugués
Realizamos medidas Mossbauer a temperatura ambiente das ligas de SM IND.2 (CO IND.1-XFE IND.X) ind.17, COM X = 0.1 A 0.6, E DAS LIGAS sm (CO IND.0.90-VFE IND.VCU IND.0.08ZR IND.0.02) ind.8.35, Com V variando de 0.23 A 0.27. Estas amostras foram caracterizadas por difração de raio X. elas apresentaram a estrutura romboédrica do tipo th ind.2zn ind.17 (R3barraM) com os átomos de Fe ocupando quatro sítios cristalográficos distintos todos os espectros obtidos apresentaram desdobramento magnético e um nível de complexidade alto, resultado da sobreposição de quatro sítios distintos de átomos de fe. Os espectros foram ajustados e através desse ajuste determinados os parâmetros hiperfinos associados a cada sítio e suas respectivas populações. Os resultados obtidos das populações dos sítios nas series de compostos Sm ind.2 (CO IND.1-XFE IND.X) ind.17 revelaram a forte preferência dos átomos de FE de ocupar os sítios halteres (2c). No modelo proposto por ray, à função do ZR e o de deslocar pares de FE dos sítios halteres, substituindo-os por pares ZR-vacância. Através dos resultados obtidos pudemos também comprovar esta hipótese através da análise das populações dos sítios das duas series de amostras.
Título en inglés
Analysis of populations of sites of SM2 (Co, Fe) 17 alloys by Mossbauer spectroscopy
Palabras clave en inglés
magnetic alloys SM2 CO17
Mössbauer spectroscopy
Permanent magnets
Resumen en inglés
Mössbauer measurements were carried out at room temperature for Sm2(Co1-xFex)17 alloys with x=0,1 to 0,6 and Sm2(Co0.9-vFevCu0.08Zr0.02)8.35, with v=0.23 to 0.27. All samples were characterized by X-ray diffraction. They showed rhombohedral structure of th2Zn17 type (R3m), where Fe atoms occupy four crystallographic sites. All spectra showed magnetic splitting and a high complexity resulting from the superposition of four Fe sites. Hyperfine parameters and site populations were obtained by least-squares fitting of the spectra. For Sm2(Co1-xFex)17 alloys, Fe atoms show a strong preference for 2c (dumbbell) sites. In the Zr-containing alloys, on the other hand, this tendency is significantly reduced, confirming A. E. Rays hypothesis on the role of Zr in the improvement of the magnetic properties of these alloys through metallurgical treatments.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
44262Nagamine.pdf (5.44 Mbytes)
Fecha de Publicación
2014-05-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.