• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
10.11606/D.43.2017.tde-13032017-121314
Document
Auteur
Nom complet
Marcelo Jacob da Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 1999
Directeur
Titre en portugais
Crescimento e Caracterização de Pontos Quânticos de InAs Auto-formados
Mots-clés en portugais
Matéria Condensada ; Semicondutores
Resumé en portugais
Neste trabalho, estudamos o crescimento epitaxial por feixe molecular de pontos quânticos de InAs/GaAs, bem como sua propriedades ópticas e morfológicas. O método de crescimento, em baixa taxa foi usado para a fabricação de estruturas de pontos quânticos com alturas médias suficientes para a obtenção de resposta óptica nas faixas de 1,3'mü'm e 1,5'mü'm em temperatura ambiente. O interesse na manufatura desse tipo de amostra decorre do fato de serem estes os comprimento de onda de mínima atenuação de sinal em redes de transmissão por fibras ópticas. O estudo sistemático das etapas envolvidas na evolução de pontos quânticos de superfície no regime de baixa taxa de deposição permitiu entender como tais estruturas, com alturas médias bem maiores que as normalmente obtidas na literatura, puderam ser alcançadas. As condições de crescimento foram otimizadas para a produção de emissões estreitas nas faixas de comprimento de onda
Titre en anglais
Study of the tuning of optical emission of InAs / GaAs quantum dots in the 1,3'mü'm and 1,5'mü'm regions
Mots-clés en anglais
Condensed matter
semiconductors
Resumé en anglais
In this work, we studied the evolution of InAs quantum dots grown by MBE as a function o f the amount o f material deposited. The monitoring o f the quantum-dot prope1ties during their evolution was possible because of the growth of a sample in which the thickness o f material was varied continuously on its area. The structure o f the samples used in this work consists oftwo quantmn-dot layers, one on the samples' surface and the other between GaAs barriers. The first quantum-dot layer was used in the morphological characterization, through AFM images, and the second one was probed by photoluminescense measurements. Moreover, the structure includes an InxGa1_xAs quantum well to be used as a reference. The possibility of carrying out optical and morphological measurements on the same sample provided us with a way to make comparisons between the topographical and optical features, yielding some interesting results, as the dependence of the optical emission with the surface quantum-dot coverage and its degradation when the islands density is higher than 1 ÜÜÜJ.Lm-2
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
29823_SILVA.pdf (14.45 Mbytes)
Date de Publication
2017-03-13
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.