Tese de Doutorado
DOI
10.11606/T.43.1996.tde-15082012-154441
Documento
Autor
Nome completo
Urias Echterhoff Takatohi
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 1996
Orientador
Banca examinadora
Watanabe, Shigueo (Presidente)
Bressiani, José Carlos
Martinelli, José Roberto
Pontuschka, Walter Maigon
Rouse, Colin Graham
Título em português
Preparação e Propriedades de Vidros Fotocrômicos Dopados com Cloreto de Prata
Palavras-chave em português
Absorção óptica
Fotocromismo
Saxs
Vidro
Resumo em português
Este trabalho teve por objetivo o preparo e estudo das propriedades de vidros fotocrômicos. Foram preparados vidros de aluminoborosilicatos de potássio (40'SI''O IND. 2'.10'AL IND. 2''O IND. 3'.(50-x)'B IND. 2''O IND. 3'.X'K IND. 2''O'- 14,9 < x < 17,7) dopados com 'AG''CL' e 'CU POT. 2+'. As amostras foram fundidas em cadinho de platina, em forno de elementos resistivos de 'SI''C', a '1400 GRAUS'C por duas horas, sendo derramados sobre molde de aço inoxidável. Uma tentativa de análise química quantitativa dos componentes após a fusão foi feita por Retroespalhamento de Rutherford. A proporção de prata retida no vidro foi determinada por este método. Medidas de dilatometria e densidade foram feitas para amostras de composição base diferentes. As medidas de dilatometria permitem a obtenção do coeficiente de dilatação térmica, e os parâmetros típicos de vidros conhecidos como: temperatura de transição vítrea e temperatura de "softening dilatométrico". Tratamentos térmicos em temperaturas próximas do ponto de amolecimento (softening point) provocam a precipitação de partículas coloidais de 'AG''CL' na matriz vítrea. Estas são responsáveis pelo comportamento fotocrômico dos vidros. Fatias de uma amostra foram submetidas a programas de tratamento térmico de 0,5 h a várias temperaturas entre '480 GRAUS'C e '620 GRAUS'C e programas de vários intervalos de tempo entre 0,25 e 1,25h a '600 GRAUS'C. As propriedades de absorção óptica das várias fatias, antes e depois de exposição à luz UV, foram comparadas. As características morfológicas das partículas coloidais de 'AG''CL' produzidas pelos tratamentos térmicos foram investigadas por SAXS. Os raios R das partículas mostraram uma relação linear com a temperatura para tratamentos de 0,5 h entre 550 e '620 GRAUS'C e uma relação linear de 'R POT. 3' com o tempo de tratamento a '600 GRAUS'C. Duas séries de amostras foram preparadas para estudar: 1. a influência da quantidade de cobre 2. a influência da proporção de 'K IND. 2''O' em relação a 'B IND. 2''O IND. 3'. As propriedades de absorção óptica (antes e depois de exposição à luz UV) das amostras das duas séries, submetidas a tratamentos térmicos a '600 GRAUS'C por diversos tempos entre 0,25 e 1,6 h foram comparadas.
Título em inglês
Preparation and properties of photochromic glasses doped with Silver Chloride
Palavras-chave em inglês
Glass
optical absorption
photochromism
SAXS
Resumo em inglês
The purpose of the present work was to prepare and study the properties of photochromic glasses. Potassium aluminoborosilicate glasses (40'SI''O IND. 2'.10'AL IND. 2''O IND. 3'.(50-x)'B IND. 2''O IND. 3'.X'K IND. 2''O'- 14,9 < x < 17,7) doped with 'AG''CL' and 'CU POT. 2+' were prepared. The samples were melted in platinum crucible, in electric furnace with silicon carbide resistences, at '1400 GRAUS'C for two hours, and poured on stainless steel mold. An attempt to perform a quantitative chemical analisis of the components after melting was carried out by Rutherford Backscattering method. The amount of silver incorporated into the glass was determined by this method. Measurements of dilatometry and density were performed for samples of different base composition. The dilatometric measurements give the thermal expansion coefficient, and the typical glass parameters such as glass transition point and dilatometric softening point. Thermal treatments at temperatures near the softening point precipitate colloidal 'AG''CL' particles in the glass matrix. These particles are responsible for the photochromic characteristics of the glass. Slices of a sample were submitted to thermal treatments for 0.5 hours at temperatures between 480 and '620 GRAUS'C and treatments at '600 GRAUS'C for several) time intervals between 0.25 and 1.25 hours. The optical absorption properties of these slices, before and after UV light exposure, were compared. The morphological aspects of the 'AG''CL' coloidal particles were investigated by SAXS. The particle radii R presented a linear relation with the temperature for treatments for 0.5 hour at temperatures between 550 and '620 GRAUS'C and a linear relation of 'R POT. 3' with time for treatments at '600 GRAUS'C. Two sample series were prepared to investigate: 1. the influence of the amount of copper 2. the influence of the amount of 'K IND. 2''O' in relation to the amout of 'B IND. 2''O IND. 3' The optical absorbances (before and after exposure to UV light) for samples of the two series, annealed at '600 GRAUS'C for different times between 0.25 and 1.6 hours were compared.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
46150Takatohi.pdf (41.76 Mbytes)
Data de Publicação
2012-08-15
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2022. Todos os direitos reservados.