Disertación de Maestría
DOI
10.11606/D.3.2008.tde-17112008-161426
Documento
Autor
Nombre completo
Renato Luiz Lehnert Portela Cerveira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Batalha, Gilmar Ferreira (Presidente)
Moura Neto, Carlos de
Stipkovic Filho, Marco
Título en portugués
Caracterização experimental do comportamento mecânico sob solicitação multiaxial em junções de chapas AA2024-T3 soldadas por fricção-mistura ('FSW').
Palabras clave en portugués
Alumínio
Ligas leves
Processos de fabricação (engenharia mecânica)
Resistência dos materiais
Soldagem
Resumen en portugués
Este trabalho tem o intuito de analisar a junção realizada pelo processo de soldagem por fricção-mistura (FSW) pelo do teste de Arcan. É apresentada inicialmente uma revisão bibliográfica dos estudos já realizados nessa área e da teoria relevante. Foram realizados ensaios para avaliar a falha da junta sob carregamento multiaxial quando comparada à falha do material base. Para a realização dos ensaios utilizouse uma máquina de tração com capacidade de 50 kN. Foi projetado e construído um dispositivo de Arcan modificado, que permite a variação do ângulo com o qual a força de tração é aplicada. Os resultados práticos demonstraram as características de resistência da junção por FSW quando sujeita à forças de tração e cisalhamento. Os resultados obtidos servem como base para comparação entre junções feitas por FSW e por métodos convencionais como a utilização de rebites (prática muito comum na indústria aeronáutica).
Título en inglés
Experimental characterization of the mechanical behaviour under multiaxial loads of AA2024-T3 sheets welded by friction stir welding (FSW).
Palabras clave en inglés
Aluminum
Light alloys
Manufacturing processes
Mechanical engineering
Strength of materials
Welding
Resumen en inglés
The aim of this work is to analyze the junction made by Friction Stir Welding (FSW) using the Arcan test. Initially is presented a review of the studies carried out in this area and the relevant theory for the project. Tests were executed in order to evaluate the failure of the welding under multiaxial loading when compared to the failure of the base material. In order to execute the Arcan Tests, a tensile test machine with nominal capacity of 50 kN was used. A modified Arcan device, that allows an angle variation of the force applied, was developed and fabricated. The practical results demonstrate the FSW joint resistance characteristics when subjected to normal and shear forces. The results obtained serve as basis to compare the junctions made using FSW and conventional joint methods like rivets (very common practice in the aeronautical industry).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-12-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.