Tesis Doctoral
DOI
https://doi.org/10.11606/T.3.2014.tde-14122014-155118
Documento
Autor
Nombre completo
Marcelo Bertolete Carneiro
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2014
Director
Tribunal
Machado, Izabel Fernanda (Presidente)
Hassui, Amauri
Hernandes, Vânia Trombini
Rodrigues, Alessandro Roger
Yoshimura, Humberto Naoyuki
Título en portugués
Fabricação de ferramentas de corte em gradação funcional por Spark Plasma Sintering (SPS).
Palabras clave en portugués
Ferramentas de corte
FGM
Sinterização
Usinagem
Resumen en portugués
O objetivo do trabalho foi fabricar ferramentas de corte para usinagem a partir de materiais em gradação funcional (Functionally Graded Materials FGM), fazendo uso da técnica de sinterização por plasma pulsado (Spark Plasma Sintering SPS), a qual permite taxa de aquecimento e resfriamento maior do que as técnicas tradicionais, menor temperatura e tempo de operação, melhor controle energético e alta repetibilidade. Os materiais utilizados foram pós cerâmicos a base de alumina (Al2O3-ZrO2 e Al2O3-TiC) e metal duro (WC-Co), de modo que dois insertos foram desenvolvidos, um de cerâmica branca (Al2O3-ZrO2) em gradação com metal duro e outro de cerâmica mista (Al2O3-TiC) em gradação com metal duro. A metodologia experimental levou em conta a aplicação de um modelo termomecânico para estimar a tensão residual térmica ao longo da espessura da ferramenta, estudo da influência dos parâmetros de sinterização por SPS (Temperatura e Pressão) sobre a qualidade do sinterizado (caracterização da propriedade física, densidade), com base nesses dados foi escolhida a melhor condição de operação para fabricar corpos de prova (CPs) para os ensaios mecânicos de resistência à flexão, dureza e tenacidade à fratura, além de insertos em FGM para os ensaios de usinagem em ferro fundido cinzento fazendo uso da operação de torneamento. Os resultados mostraram que o parâmetro de máquina que mais influenciou a densidade foi a Temperatura, os FGMs de AlTiC e AlZr obtiveram um aumento de 126 e 73% na resistência à flexão em relação às suas respectivas cerâmicas homogêneas, seguindo a sequência dos materiais, a dureza foi avaliada em 13,8 e 15,8 GPa, enquanto a tenacidade à fratura em 4,91 e 5,04 MPa.m1/2. Quanto aos ensaios de usinagem, as ferramentas de FGM AlZr apresentaram menor desgaste do que as de FGM AlTiC, as forças de corte foram influenciadas pelas variáveis Avanço e Velocidade de corte, finalmente, o Avanço foi a variável que mais influenciou os resultados de rugosidade.
Título en inglés
Fabrication of cutting tools from functionally graded materials using Spark Plasma Sintering (SPS).
Palabras clave en inglés
Cutting tools
FGM
Machining
Sintering
Resumen en inglés
The aim was fabricating cutting tools from functionally graded materials (FGM) by spark plasma sintering method (SPS), which allow heating and cooling rates higher than traditional methods, lower temperature and shorter time sintering, better energy control and high reproducibility. The materials used were ceramic powders based on alumina (Al2O3-ZrO2 and Al2O3-TiC) and cemented carbide (WC-Co), so that two inserts were developed, one of white ceramic (Al2O3-ZrO2) graded with cemented carbide and the other of mixed ceramic (Al2O3- TiC) graded with cemented carbide. The experimental methodology was developed from thermo-mechanical model application to estimate thermal residual stress along with tool thickness, study into the influence of SPS sintering parameters (Temperature and Pressure) over sintered quality (physical properties characterization, density), on the basis of these data, the best operating condition was chosen to fabricate workpieces for mechanical tests of flexural strength, hardness and fracture toughness, besides FGM inserts to machining tests in grey cast iron using turning operation. The results showed the machine parameter that mostly influenced density was Temperature; the AlTiC and AlZr FGMs got an increase of 126 and 73% in flexural strength in relation to their homogeneous ceramics. Following the materials sequence, the hardness was evaluated at 13.8 and 15.8 GPa, whereas the fracture toughness was 4.91 and 5.04 MPa.m1/2. For the machining tests, FGM AlZr cutting tools showed lower wear than FGM AlTiC ones; the cutting forces were influenced by Feed Rate and Cutting Speed. Finally, the Feed Rate was the variable that mostly influenced the roughness results.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-01-08
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • Bertolete Carneiro, Marcelo, Machado, Izabel Fernanda, e Rodrigues, Daniel. Analysis of Sintering Parameters by SPS on Cemented Carbide [doi:10.4028/www.scientific.net/AMR.223.579]. Advanced Materials Research [online], 2011, vol. 223, p. 579-587.
  • CARNEIRO, MARCELO BERTOLETE, and Machado, Izabel Fernanda. Sintering and Model of Thermal Residual Stress for Getting Cutting Tools from Functionally Gradient Materials [doi:10.1016/j.procir.2013.06.089]. Procedia CIRP [online], 2013, vol. 8, p. 199-204.
  • CARVALHO, E. de, et al. Caracterização da perovskita CaCu3Ti4O12 consolidada por sinterização assistida por campo elétrico. Cerâmica (São Paulo. Impresso) [online], 2013, vol. 59, p. 293-301. Dispon?vel em: http://www.scielo.br/cgi-bin/wxis.exe/iah/.
  • GOVEA-ALCAIDE, E., et al. Consolidation of Bi-2223 superconducting powders by spark plasma sintering [doi:10.1063/1.4768257]. Journal of Applied Physics [online], 2012, vol. 112, p. 113906.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.