Pozolanicidade do metacaulim em sistemas binários com cimento Portland e hidróxido de cálcio.
Palabras clave en portugués
Cimento pozolânico
Concreto
Hidróxido de cálcio
Metacaulim
Pasta
Resumen en portugués
O metacaulim é um material pozolânico que vem sendo pesquisado e adotado em vários países. O metacaulim é constituído basicamente de sílica (SiO) e alumina (Al2O3) na fase amorfa, capaz de reagir com o hidróxido de cálcio Ca(OH) gerado durante a hidratação do cimento Portland, formando produtos hidratados similares aos decorrentes da hidratação direta do clinquer Portland. Esta pozolana acelera o processo de hidratação do cimento, formando silicato de cálcio hidratado (C-S-H) adicional. O conhecimento das características do metacaulim que influenciam a interação com a cal, se faz necessário para subsidiar medidas preventivas com relação ao consumo de portlandita. O presente trabalho visa determinar as características físico-químicas relevantes para o entendimento da atividade pozolânica, avaliando as reações propiciadas pelo metacaulim em sistemas binários. Para este propósito, realizaram-se estudos experimentais em pasta e concreto, usando as técnicas de difratometria de raios X e de termogravimetria. As etapas experimentais consistiram: na caracterização do metacaulim, com ênfase na determinação do teor da fase amorfa; a avaliação da cinética da reação em sistema metacaulim/hidróxido de cálcio e análise da evolução da hidratação de cimento com alto teor de metacaulim. Nos sistemas cimenticios de concretos com diferentes teores de substituição de metacaulim com e sem cal hidratada, foi avaliado o comportamento da resistência à compressão. No metacaulim estudado, o teor da fase amorfa foi de 74,60% e o restante (25,40%) atua como material inerte, e o consumo máximo por atividade pozolânica, foi de 1,34 gr de Ca(OH)/grama de fase amorfa de metacaulim. Na evolução das reações, por atividade pozolânica o C-S-H foi formando gradativamente. A adição de 15% de metacaulim e 5% de cal hidratada em concretos proporcionou um ganho de resistência de 17% a mais em função do concreto de referência.
Título en inglés
Pozzolanic metakaolin in the binary systems with Portland cement and calcium hidroxide.
Palabras clave en inglés
Calcium hidroxide
Concrete
Metakaolin
Paste
Pozzolanic cement
Resumen en inglés
The metakaolin is a pozzolanic material that has been investigated and adopted in several countries. The metakaolin consists primarily of silica (SiO) and alumina (Al2O3) in the amorphous phase, and can react with calcium hydroxide Ca (OH) generated during hydration of Portland cement to form products similar to those obtained during Portland clinker basic hydration. This pozzolana could accelerate the hydration of cement, forming calcium silicate hydrate (C-S-H) additional. The knowledge of the characteristics of metakaolin that influence the interaction with lime provides the necessary subsidize to prevent excessive consumption of portlandite. This paper aims to determine the physical and chemical relevant characteristics in order to understand the pozzolanic activity, evaluating the responses provided by the metakaolin in binary systems. For this purpose, experimental studies were conducted in paste and concrete, using the techniques of X-ray diffraction and thermogravimetry. The experimental steps consisted of: the characterization of metakaolin, with emphasis on determining the amorphous phase content, this evaluation of the kinetics of the reaction system metakaolin and calcium hydroxide; The analysis of the evolution of the cement hydration with high content of metakaolin. In cementitious systems of concrete with different metakaolin replacement levels with and without hydrated lime, was rated the behavior of the compressive strength. The content of amorphous phase In the studied metakaolim was 74.60% and the remainder (25.40%) acts as an inert material, and the máximum consumption by pozzolanic activity was 1.34 g of Ca (OH)/g amorphous phase of metakaolin. During the evolution of pozzolanic reactions, the C-S-H was gradually formed. The addition of 15% metakaolin and 5% hydrated lime in concrete has a strength gain of 17% more depending on the reference concrete.
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-04-09