Mémoire de Maîtrise
DOI
10.11606/D.3.2002.tde-05112002-172710
Document
Auteur
Nom complet
Aluizio Caldas e Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2002
Directeur
Jury
John, Vanderley Moacyr (Président)
Armelin, Hugo Sogayar
Savastano Junior, Holmer
Titre en portugais
Estudo da durabilidade de compósitos reforçados com fibras de celulose.
Mots-clés en portugais
carbonatação
compósitos
durabilidade
ensaios de envelhecimento
escória de alto-forno
fibras de celulose
Resumé en portugais
O uso de fibras vegetais e de cimentos alternativos – ambos provenientes de resíduos, é tido como boa opção na busca por novos fibrocimentos. Entretanto, a maioria das pesquisas desenvolvida nos últimos anos tem apresentado resultados desanimadores no que se refere à durabilidade do material. Além disso, os métodos para avaliação do desempenho ao longo do tempo de materiais reforçados com fibras sensíveis a álcalis ainda não estão bem estabelecidos. O trabalho avaliou o comportamento de compósitos produzidos com cimento de escória de alto-forno reforçados com fibras de celulose, moldados através de adaptações dos processos industriais usados em todo mundo pelas empresas de fibrocimento. Em seguida, a durabilidade das formulações foi avaliada através de ensaios de envelhecimento, os quais se basearam na simulação dos principais agentes e mecanismos de degradação atuantes no material. O desempenho físico e mecânico dos compósitos foi avaliado através da análise de propriedades pré-estabelecidas, consideradas importantes no emprego material como componente construtivo. A análise dos resultados confirmou a eficiência da incorporação da celulose nas propriedades mecânicas do compósito. A durabilidade do material foi diferente para as matrizes empregadas. As matrizes ativadas com gipsita e cal hidratada (EGCH) foram menos agressivas às fibras, entretanto apresentaram problemas de hidratação às primeiras idades e perda de resistência devido à carbonatação. A matriz ECP, mais alcalina, apresentou resultados superiores de resistência mecânica nas primeiras idades. Ela decompôs as fibras e reduziu as propriedades mecânicas durante o envelhecimento. A carbonatação reduziu o ataque alcalino às fibras nestas matrizes, estabilizando a resistência mecânica e a perda de tenacidade não foi tão acentuada. A metodologia de envelhecimento acelerado que combinou ciclos de molhagem e secagem à carbonatação se mostrou eficiente na simulação do envelhecimento natural.
Titre en anglais
Durability of cellulose fibers reinforced composites.
Mots-clés en anglais
blast-furnace slag
carbonation
cellulose fibers
composites
durability
pulps
weathering
Resumé en anglais
Vegetable fibers and alternative cements from residues is a good option for replacement asbestos-cement. However, research development has presented no satisfactory results concerning material durability and methods of performance evaluation to reinforced materials with alcali sensitive fibers are not well developed. The objetives of this research are: a) evaluation of composites behavior produced with blast-furnace slag reinforced with residual cellulose fibers, which were moulded in adapted conventional industrial processes, common in fibercement companies around world and b) durability performance evaluation applying proposed aging tests. Aging tests were based on simulation of main agents and degradation mechanisms. Physical and mechanical behaviour of composites was evaluated considering important properties in building component uses. Cellulose fibers improved the mechanical properties of the composites. Durability presented different results for the two matrices. The matrices activated with gypsum and hidrated lime (EGCH) have been less aggressive than matrix activated with ordinary Portland cement (OPC) in relation to fibers. However, they presented problems concerning to the hydration at early dates and loss of resistance due to carbonation. Matrices activated with OPC presented better results of MOR at the early dates. In fact, they are more alkaline and they decomposed fibers and reduced the mechanical properties during the aging. The carbonation reduced the alkaline attack, stabilizing the MOR and reducing the loss of tenacity. The accelerated methods with carbonation were efficient in the simulation of the natural ageing.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Aluizio.pdf (4.21 Mbytes)
Date de Publication
2002-12-10
 
AVERTISSEMENT: Le matériau se réfère à des documents provenant de cette thèse ou mémoire. Le contenu de ces documents est la responsabilité de l'auteur de la thèse ou mémoire.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.