Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.2020.tde-04032021-110133
Document
Auteur
Nom complet
Ronney Rodrigues Agra
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2020
Directeur
Jury
Figueiredo, Antonio Domingues de (Président)
Rambo, Dimas Alan Strauss
Silva, Flávio de Andrade
Titre en portugais
Influência da temperatura no comportamento do concreto com diferentes teores de fibras de aço.
Mots-clés en portugais
Concreto reforçado com fibras
Estruturas (Comportamento estrutural)
Fogo
Resistência pós fissuração
Temperaturas elevadas
Resumé en portugais
Medidas de proteção e combate ao incêndio de estruturas de concreto são foco de pesquisas em escala mundial. Sabe-se que a utilização de microfibras poliméricas promove redução no processo de lascamento explosivo do concreto e que sua combinação com fibras de aço promove efeitos benéficos em termos de resistência ao fogo. Entretanto, não há abordagem de normas, projetos e recomendações para o concreto reforçado com fibras (CRF) aplicado em estruturas quando sujeito a incêndio. Nesse contexto, o presente trabalho auxilia na parametrização do comportamento estrutural do CRF submetido a elevadas temperaturas, à medida que avalia a capacidade de reforço proporcionado pelas fibras de aço nestas condições. Neste estudo, o aquecimento do CRF foi realizado em forno elétrico e, também, por meio da exposição unifacial ao fogo. A avaliação do comportamento mecânico pós-fissuração das amostras submetidas a elevadas temperaturas e dosadas com teores distintos de fibras de aço (20, 35 e 70 kg/m³, o que corresponde, em volume, a 0,26%, 0,45% e 0,90%, respectivamente) foi realizada por meio dos ensaios DEWS (Double Edge Wedge Splitting) e de flexão de três pontos. Apesar da deterioração intensa da resistência à compressão do CRF, sua taxa de degradação ocorreu de forma distinta com a elevação da temperatura, em função do teor de fibras de aço empregado, de modo que amostras com baixos teores apresentaram reduções mais intensas em relação às amostras com teores elevados. A principal preocupação é quanto à resistência à tração, que é significativamente afetada em temperaturas acima de 300 ºC. No entanto, também foi constatado efeito positivo proporcionado pelo aumento do teor de fibras, de forma que diminuíram as taxas de degradação nessa propriedade. Além disso, foi constatada a influência direta do aumento do teor de fibras na capacidade resistente pós-fissuração do compósito. Com o aumento da temperatura, as fibras perderam sua capacidade de reforço e, assim, ocorreram reduções gradativas na capacidade resistente residual, de modo que após 600 °C, o CRF conservava apenas 20% e 30% da sua resistência à tração pós-fissuração associada ao estado limite de serviço (ELS) e estado limite último (ELU) respectivamente, independente do teor de fibras. Após exposição ao fogo, os valores de resistência à tração da matriz e resistência à tração pós-fissuração associados ao ELU tenderam aos resultados obtidos para a temperatura de 450°C, independente do teor de fibra empregado. Os resultados obtidos poderão ser utilizados para a elaboração de equações constitutivas e servem como dados de entrada em modelos numéricos de previsão de comportamento estrutural de elementos executados com CRF.
Titre en anglais
Influence of temperature on the behavior of concrete with diferent fiber content.
Mots-clés en anglais
Elevated temperatures
Fire resistance
Post-crack tensile strength
Steel fiber reinforced concrete
Structural behavior
Resumé en anglais
Fire protection and firefighting measures for concrete structures are research topics in a worldwide scale. It is known that the use of micro-synthetic fibers reduces the occurrence of explosive spalling, and that its use with steel fibers promotes beneficial effects in terms of fire resistance. However, the current standards and recommendations do not provide an adequate approach regarding the use of fiber reinforced concrete (FRC) for structural applications under fire. In this context, the present work aids in the parameterization of the structural behavior of the FRC subjected to high temperatures, as it assesses the reinforcement capacity provided by steel fibers. The heating procedure was conducted using an electric oven, for target temperatures, and a vertical fire simulator that induced a single-surface fire exposure. The post-crack mechanical behavior of samples subjected to high temperatures and produced with different fiber contents (20, 35 and 70 kg / m³, which corresponds, in volume, to 0.26%, 0.45% and 0.90%, respectively) was performed using the DEWS (Double Edge Wedge Splitting) test and the classical three-point bending test. Despite the intense deterioration of the FRC compressive strength, the rate of degradation under temperature was reduced for higher contents of steel fibers. The main concern is related to the tensile properties, which are affected for temperatures above 300 ºC. However, the increase in fiber content mitigated the degradation rate in the tensile properties of the material. In addition, the influence of the fiber content on the post-crack behavior was characterized. As the temperature increased, the fibers lost their reinforcement capacity and a gradual reduction in the post-crack properties was verified, in which the FRC exposed to 600 °C retained only 20% and 30% of its post-cracking tensile strength at crack openings relative to service limit state (SLS) and ultimate limit state (ULS), respectively, regardless of the fiber content. After exposure to fire, the matrix tensile strength and the ULS post-crack tensile strength tended to the results obtained for the temperature of 450 ° C, regardless of the fiber content used. The results obtained may be used for the elaboration of constitutive equations and serve as input data in numerical models that aim to predict the structural behavior of FRC elements.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2021-03-10
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.