Disertación de Maestría
DOI
10.11606/D.3.2012.tde-23032012-115636
Documento
Autor
Nombre completo
Fábio Izumi
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2012
Director
Tribunal
Kassab, Luciana Reyes Pires (Presidente)
Alayo Chávez, Marco Isaías
Siarkowski, Acácio Luiz
Título en portugués
Produção e caracterização de filmes finos amorfos para aplicações em dispositivos fotônicos.
Palabras clave en portugués
BWT
Filmes finos
Fotônica
Guia de onda
Sputtering
Vidro
Resumen en portugués
O presente trabalho possui como objetivo o estudo das propriedades dos filmes finos amorfos para aplicações em dispositivos fotônicos. Foram produzidos, por meio da técnica sputtering, filmes finos de telureto BWT, a partir de alvos cerâmicos com composição em peso de 54,6 TeO2 - 22,6 WO3 - 22,8 Bi2O3. A escolha dos vidros BWT se deve às qualidades elétricas e ópticas dos teluretos. Filmes com nanopartículas de ouro foram produzidos e a nucleação das nanopartículas se deu por tratamento térmico. Os filmes produzidos foram caracterizados pelas técnicas de elipsometria, perfilometria, espectrometria de fluorescência de raios-X por energia dispersiva, difração de raios-X, transmissão, absorção e microscopia eletrônica de transmissão e de varredura. Como etapa, final foram produzidos guias de onda do tipo rib por meio de procedimentos de corrosão e litografia, a fim de que fossem testados guiamentos de luz em 632,8 nm e em 1050 nm. Foram usados diferentes fluxos de SF6 para corrosão dos filmes, resultando em guias de diferentes valores de h_core. Os guias com h_core de 63 e 82 nm apresentaram perda de no máximo 3,5 dB/cm para guiamento em 632,8 e 1050 nm em guias com larguras que variaram de 6 a 10 m. As simulações realizadas mostraram guiamento multímodo para todos os casos. O material BWT é, portanto, promissor para aplicações em dispositivos fotônicos.
Título en inglés
Production and characterization of amorphous thin films to applications in photonic devices.
Palabras clave en inglés
BWT
Glass
Photonics
Sputtering
Thin films
Waveguide
Resumen en inglés
The objective of this present work is study the properties of amorphous thin films for applications in photonic devices. Thin films of tellurite BWT were produced by sputtering technique using targets whose compositions in weight are 54.6 TeO2 - 22.6 WO3 - 22.8 Bi2O3. BWT was chosen due to the electrical and optical properties of tellurite. Films with gold nanoparticles were produced and the nucleation of the nanoparticles was obtained by heat treatment. Films were characterized by the techniques of elipsometry, perfilometry, energy dispersive X-ray spectroscopy, X-ray diffraction, absorption, transmission, scanning electronic and transmission electronic microscopies. The final step was production of BWT rib waveguides using lithography and reactive-ion etching in order to test light guiding at 632.8 nm and 1050 nm. BWT rib waveguides were produced, using different flux of SF6 for the etching, resulting in waveguides with different values of h_core. Waveguides with 63 and 82 nm of h_core presented maximum loss of 3,5 dB/cm at 632.8 nm and 1050 nm wavelengths in guides with widths ranging from 6 to 10 m. All simulations showed multimode guiding. The BWT material is a potential candidate for applications in photonic devices.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-04-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.