Disertación de Maestría
DOI
10.11606/D.3.2006.tde-22072007-172649
Documento
Autor
Nombre completo
Ricardo Luís Ohta
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Morimoto, Nilton Itiro (Presidente)
Fonseca, Fernando Josepetti
Gonçalves Neto, Luiz
Título en portugués
Construção e caracterização de fotodetetores metal-semicondutor-metal (MSM).
Palabras clave en portugués
Dispositivos ópticos
Fabricação (microeletrônica)
Semicondutores
Resumen en portugués
Este trabalho teve como objetivo principal a fabricação de fotodetetores do tipo Metal-Semicondutor-Metal (MSM) com corrente de escuro da ordem de 1 nA, responsividade da ordem de 0,1 A/W e razão fotocorrente/corrente de escuro de pelo menos 10. Estes valores asseguram que os fotodetetores obtidos tenham sensibilidade suficiente para serem utilizados em sensores ópticos integrados. Todos os materiais utilizados na construção dos fotodetetores MSM são compatíveis com processos convencionais de fabricação em microeletrônica, facilitando a integração com outros dispositivos em estado sólido. O semicondutor utilizado nos fotodetetores foi o silício, na forma monocristalina ou policristalina. Como material de eletrodo, foi utilizado o alumínio, o titânio ou o níquel. No processo de fabricação básico, foram utilizados apenas três etapas: deposição do filme metálico, fotolitografia e corrosão, confirmando a simplicidade de fabricação desse fotodetetor. Através da construção de dispositivos com diferentes geometrias e diferentes combinações dos materiais citados acima, foi possível verificar a influência que a estrutura cristalina do semicondutor, tipo de dopagem do semicondutor, geometria e material de eletrodo tem sobre o desempenho e o comportamento dos MSMs. O comprimento de onda de 632,8 nm foi utilizado na caracterização dos dispositivos, devido a sua disponibilidade e o desenvolvimento de guias ópticos utilizando esse comprimento de onda em trabalhos anteriores do nosso grupo de pesquisa. Os melhores resultados obtidos foram com as amostras de Si monocristalino tipo-p com eletrodos de titânio. Na amostra sinterizada à 250°C foi obtido um valor da corrente de escuro de 4,8 nA e, na amostra de referência, foi obtido um valor de responsividade de 0,28 A/W.
Título en inglés
Construction and characterization of metal-semiconductor-metal (MSM) photodetectors.
Palabras clave en inglés
Fabrication (microelectronic)
Optic devices
Semiconductor
Resumen en inglés
The goal of this work was the fabrication of Metal-Semiconductor-Metal (MSM) photodetectors with the following characteristics: dark current of about 1 nA, responsivity of about 0.1 A/W and dark/photocurrent ratio of at least 10. These values ensure that the photodetectors have enough sensitivity to be used in integrated optic sensors. All materials used in the fabrication of the MSM are compatible with conventional microelectronic manufacture process, so that the photodetectors can be more easily integrated with other solid-state devices. The semiconductor used in the photodetectors was silicon, in single crystal and polycrystalline form. As material of electrodes, aluminum, titanium or nickel had been used. The basic fabrication process consists of only three steps: metal film deposition, photolithography and etching, which confirm the simplicity of the fabrication of this device. Building MSMs with different geometries and making combinations with the materials cited above, gave the possibility to verify the influence that crystalline structure of the semiconductor, doping type of the semiconductor, geometry and electrode material have on the behavior of the photodetectors. The wavelength of 632.8 nm was used in the characterization of the devices, due to its availability and the development of optic waveguides using this wavelength in previous works of our research group. The best results were obtained with the samples fabricated using single crystal Si p-type with titanium electrodes. The sample annealed at 250°C had dark current value of 4.8 nA and, the reference sample had responsivity of 0.28 A/W.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2007-08-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.