Dissertação de Mestrado
DOI
10.11606/D.3.2012.tde-18062013-154723
Documento
Autor
Nome completo
Tiago Marques Fraga
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2012
Orientador
Banca examinadora
Pereyra, Inés (Presidente)
Onmori, Roberto Koji
Souza, Flavio Leandro de
Título em português
Produção de nanotubos de TiO2 visando sua aplicação em células solares.
Palavras-chave em português
Células solares
Dispositivos foto-voltáicos
Nanotubos de TiO2
Resumo em português
Nesse trabalho foram obtidos nanotubos de TiO2 pelo processo de anodização do titânio em soluções fluoradas visando sua aplicação em células solares, pois estes apresentam melhores propriedades que o TiO2 em forma de filme fino ou de nanopartículas, devido a sua maior área superficial e melhores propriedades de transporte de carga. Os processos de anodização foram realizados em lâminas de titânio com soluções de HF e NH4F e diferentes tensões e tempos de anodização, pois a tensão elétrica aplicada no processo pode ser utilizada para controlar o diâmetro, espessura e comprimento dos nanotubos. As amostras obtidas com as soluções de NH4F foram as que apresentaram os melhores resultados, com tubos de paredes mais lisas, comprimentos maiores e forma mais definida, pois as soluções de NH4F apresentam menor taxa de corrosão que as soluções de HF. Portanto, nesse trabalho as soluções de NH4F também foram utilizadas para crescer nanotubos sobre substratos de vidro, onde foi possível obter matrizes de nanotubos altamente ordenadas, e formar matrizes de nanotubos com padrões geométricos, para aplicação em células solares, sensores integráveis e cristais fotônicos. Porém nesse trabalho, os nanotubos foram utilizados somente para fabricar as células solares sensibilizadas por corante. Foram produzidas células solares utilizando lâminas de vidro cobertas por ITO e FTO, lâminas de titânio sem polimento, lâminas de Ti eletropolidas e também lâminas polidas utilizando polimento químico. Os processos de eletropolimento e polimento químico foram realizados para a obtenção de matrizes de nanotubos mais uniformes e células solares mais eficientes, utilizando esses processos foi possível obter células solares com curvas de J - V bem definidas e com fator de preenchimento (FF) de 0,5.
Título em inglês
Production of nanotubes for their application in solar cells.
Palavras-chave em inglês
Nanotubes
Solar cells
TiO2
Resumo em inglês
In this work TiO2 nanotube arrays were obtained by anodization of titanium foils in fluoride-based electrolytes, aiming their application in solar cells, due to its improved proprieties compared to TiO2 thin films or nanoparticles as a consequence of their large surface area and good electron transport. The anodization processes were performed utilizing HF and NH4F solutions with different anodization voltages and times, in order to study the effect of these parameters in the arrays morphology and structure. The samples obtained from NH4F solutions presented better results, with nanotubes exhibiting smoother walls, enhanced length and well defined shape, due to the lower NH4F solution etching rate compared to HF solution. Therefore the NH4F solutions were also utilized to grow nanotubes on glass substrates, allowing to obtain highly oriented of nanotubes arrays. Also patterned nanotube arrays were obtained for integrated sensors and photonic crystals applications. However, in this work, the nanotubes were only used to manufacture the dye sensitized solar cells. Were performed solar cells with glass substrates coating by thin films of ITO and FTO, unpolished titanium foils, eletropolished Ti foils and chemical polished Ti foils. The eletropolishing and chemical polishing process was performed to obtain more uniform nanotube arrays and more efficient solar cells, with well defined J-V curve and FF of 0,5.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
sumario_dissert_corr.pdf (186.28 Kbytes)
Data de Publicação
2013-06-28
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • FRAGA, T. M., et al. TiO2 Nanotubes Production and Characterization [doi:10.1149/04901.0199ecst]. ECS Transactions [online], 2012, vol. 49, p. 199-205.
  • FRAGA, TIAGO M., PEREYRA, INE'S, and ALBERTIN, KATIA F. Production of TiO [doi:10.1149/1.3615186]. In 26th Symposium on Microelectronics Technology and Devices (SBMicro 2011), Joao Pessoa. , 2011.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.