Disertación de Maestría
DOI
10.11606/D.3.2007.tde-14012008-103221
Documento
Autor
Nombre completo
Amanda Rossi Mascaro
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Morimoto, Nilton Itiro (Presidente)
Borges, Ben-Hur Viana
Santos Filho, Sebastião Gomes dos
Título en portugués
Fabricação de canaletas em substratos de silício para acoplamento fibra-guia utilizando siliceto de níquel como material de máscara.
Palabras clave en portugués
Microeletrônica - processos em microeletrônica
Óptica integrada - acoplamento óptico
Resumen en portugués
Neste trabalho, apresentamos um novo processo de fabricação para a obtenção de canaletas em V em substratos de silício monocristalino (100) para um acoplamento óptico utilizando siliceto de níquel como material de máscara. O filme de siliceto de níquel (10nm de espessura para 200 nm de nickel) foi obtido por processos de evaporação térmica e posterior recozimento a baixas temperaturas ( 200 e 250°C). As canaletas em V (com profundidade de 60 mm) foram fabricadas através do processo de corrosão anisotrópica, utilizando uma solução de KOH (27%-60°C). Durante este processo, a taxa de corrosão do substrato de silício pela solução de KOH foi estimada como sendo 33.1 micrômetros/h. A composição da camada de siliceto de níquel obtida foi investigada utilizando a técnica RBS, que nos forneceu a estequiometria Ni2Si. A rugosidade de filmes de níquel e de Ni2Si foi medida pela técnica AFM. Uma análise SEM foi feita com as canaletas e guias de onda obtidos. Após o processamento das canaletas em V, elas foram alinhadas com um guia de onda simples de teste para um futuro acoplamento óptico.
Título en inglés
Fabrication of V-grooves on silicon substrates for fibre-guide coupling using nickel silicide as mask material.
Palabras clave en inglés
Integrated optics
Microeletronic processes
Resumen en inglés
In this work, we present a new fabrication process to obtain V-grooves on monocrystaline silicon substrates (100) for optical coupling using nickel silicides as mask material. The nickel silicide film 10 nm thick for 200 nm of nickel thick) was obtained using thermal evaporation and annealing processes at low temperatures (200 and 250°C) as mask for alkaline solutions. Vgrooves (60 mm deep) were fabricated by anisotropic etching process, using a KOH (27%-60°) solution. During this process, the etch rate of the silicon substrate by the KOH solution was measured as 33.1 micrometers/h. The composition of the obtained nickel silicide layer was investigated using RBS technique, which supplied us the stoichiometric Ni2Si. The roughness of nickel and Ni2Si layers was measured by AFM technique. A SEM analysis was made with the obtained Vgrooves and waveguides. After processing the V-grooves, they were aligned with a simple waveguide for a future optical coupling.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-02-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.