Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.2016.tde-30062016-090801
Documento
Autor
Nombre completo
Helio Giannini
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Vianna Junior, Ardson dos Santos (Presidente)
Giudici, Reinaldo
Palma, Mauri Sergio Alves
 
Título en portugués
Polimerização em emulsão de estireno em microrreator.
Palabras clave en portugués
Emulsão
Microrreator
Poliestireno
Polimerização
Resumen en portugués
A polimerização em emulsão de estireno em um microrreator Syrris de 250 µL com misturador estático junção "T" foi estudada em duas etapas. Primeiro somente a fluidodinâmica deste dispositivo não convencional foi avaliada, depois, foi desenvolvida a reação de polimerização de forma a observar como este fator influencia no sistema. Os experimentos foram realizados procurando se atingir maiores conversões, mas mantendo a estabilidade da emulsão. Foi um trabalho exploratório, portanto se assemelha mais a um processo de evolução (evolutionary process). Foram verificados a partir de qual relação das vazões dos dois fluidos ocorre a formação de gotas, e que com o aumento da vazão da fase contínua, aquosa (Qc), mantendo constante a vazão da fase dispersa (Qd), foi verificado uma diminuição do diâmetro das gotas e um regime de fluxo laminar. Posteriormente, realizou-se a polimerização em emulsão do estireno no microrreator, porém com restrições para altas vazões. Os parâmetros de processo testados foram a proporção Qc e Qd, a temperatura e a concentração do iniciador para então verificar o efeito que a variação destas ocasionam na conversão de monômero, no diâmetro e número de partículas e nas massas moleculares médias. A polimerização foi feita para soma das vazões Qc e Qd da ordem de 100 µ L/min, com 15% de monômero na formulação e com o maior tempo de residência possível de 2,5 minutos. Para maiores concentrações de monômero, acima de 15% foi verificado entupimento do canal do microrreator. A taxa de conversão de monômero aumentou com o aumento da temperatura e com o aumento da concentração do iniciador, mas o maior valor atingido foi de apenas 37% devido ao baixo tempo de residência. Nos casos de maiores taxas de conversão, as massas moleculares obtidas foram as menores conforme o esperado pela teoria. Finalmente, os índices de polidispersão (PDI), obtidos foram da ordem de 2,5 a 3,5.
 
Título en inglés
Emulsion polimerization of styrene in microrreactor.
Palabras clave en inglés
Emulsion
Microreactor
Polymerization
Polystyrene
Resumen en inglés
The emulsion polymerization of styrene in a microreactor Syrris 250 µL with static mixer junction "T" was studied in two steps. First, only the fluidynamics of this nonconventional device was evaluated, after the polymerization reaction was developed in order to observe how this factor influencing the system. The experiments were performed seeking to achieve higher conversions, keeping the stability of the emulsion. It was an exploratory work therefore is more like an evolutionary process. The ratio of two-phase flow rates was analyzed from which of them occurs droplet formation. The flow rate of dispersed phase (Qd) was kept constant and the continuous phase (Qc), was increased. It can be observed the decreasing of droplet diameter and a laminar flow regime. Later, it was carried out emulsion polymerization of styrene in the microreactor with restrictions for high flow rates. The process parameters were analyzed: the ratio Qc/Qd, the temperature and initiator concentration and then determine the effect that these variations cause the monomer conversion, the diameter, number of particles and the average molecular weight. The polymerization occurred to the sum of the flow rates Qc and Qd of around 100 µ L/min with 15% monomer in the formulation with the highest residence time of 2,5 minutes. For higher concentrations of monomer, above 15% was observed clogging in the microreactor channel. The monomer conversion rate raised with increasing temperature and with the concentration of initiator, but the largest value achieved was only 37% due to the low residence time. In this case, the molecular weights obtained were smaller as expected by theory. Finally, the polydispersity indexes obtained were around 2.5 to 3.5.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-06-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores.
CeTI-SC/STI
© 2001-2024. Biblioteca Digital de Tesis y Disertaciones de la USP.